Examination of a Low-Temperature Rhodium Oxidation Mechanism Научная публикация
Журнал |
Kinetics and Catalysis
ISSN: 0023-1584 , E-ISSN: 1608-3210 |
||
---|---|---|---|
Вых. Данные | Год: 1994, Том: 35, Номер: 5, Страницы: 722-727 Страниц : 6 | ||
Ключевые слова | SUPPORTED RHODIUM; OXIDE FORMATION; CATALYSTS; REDUCTION; SURFACES | ||
Авторы |
|
||
Организации |
|
Реферат:
The interaction of O2 with Rh(100) and polycrystalline rhodium at O2 pressures of 10(-5) - 10(3) Pa at 400 - 600 K is studied by thermodesorption and Auger electron spectroscopy. At P(O)2 = 10(-5) - 10(-1) Pa, a surface rhodium oxide is formed, whereas at P(O)2 greater-than-or-equal-to 10(-1) Pa, a bulk rhodium oxide (Rh2O3) is produced. The bulk oxide film grows by the Cabrera-Mott mechanism of low-temperature metal oxidation. The film growth is dependent on P(O)2 and the sample temperature. The data obtained indicates that the rhodium surface structure has a minor influence on the oxidation process.
Библиографическая ссылка:
Salanov A.N.
, Savchenko V.I.
Examination of a Low-Temperature Rhodium Oxidation Mechanism
Kinetics and Catalysis. 1994. V.35. N5. P.722-727. WOS РИНЦ
Examination of a Low-Temperature Rhodium Oxidation Mechanism
Kinetics and Catalysis. 1994. V.35. N5. P.722-727. WOS РИНЦ
Оригинальная:
Саланов А.Н.
, Савченко В.И.
Механизм низкотемпературного окисления родия
Кинетика и катализ. 1994. Т.35. №5. С.780-785. РИНЦ
Механизм низкотемпературного окисления родия
Кинетика и катализ. 1994. Т.35. №5. С.780-785. РИНЦ
Даты:
Поступила в редакцию: | 30 окт. 1993 г. |
Опубликована в печати: | 1 сент. 1994 г. |
Идентификаторы БД:
Web of science | WOS:A1994PR89200022 |
РИНЦ | 30596612 |