Effect of Fe/Ni Catalyst Composition on Nitrogen Doping and Field Emission Properties of Carbon Nanotubes Научная публикация
Журнал |
Carbon
ISSN: 0008-6223 , E-ISSN: 1873-3891 |
||||||
---|---|---|---|---|---|---|---|
Вых. Данные | Год: 2008, Том: 46, Номер: 6, Страницы: 864-869 Страниц : 6 DOI: 10.1016/j.carbon.2008.02.009 | ||||||
Ключевые слова | N-2ENCAPSULATION; XPS | ||||||
Авторы |
|
||||||
Организации |
|
Информация о финансировании (1)
1 | Российский фонд фундаментальных исследований | 06-03-32816 |
Реферат:
Nitrogen-doped carbon (CNx) nanotubes have been synthesized by acetonitrile vapor decomposition over catalyst nanoparticles produced in the result of thermolysis of solid solutions of Fe and Ni bimaleates. X-ray photoelectron spectroscopy revealed the nitrogen content in CNx nanotubes grows from 0.4 to 1.2 at%, when Ni portion in catalyst increases. Nitrogen doping level of sample produced using bimaleates of Fe and Ni taken in a ratio of 7:3 is deviated from this dependence due to formation of two phases of metallic catalyst. N1s-edge X-ray absorption spectra of samples showed three peaks, which by results of quantum-chemical calculation on nitrogen-containing carbon nanotube (CNT) model were assigned to pyridinic, graphitic, and molecular forms of nitrogen. Measurements of current–voltage characteristics of the samples found the electron emission threshold is reduced with amount of nitrogen incorporated into CNx nanotubes.
Библиографическая ссылка:
Bulusheva L.G.
, Okotrub A.V.
, Kudashov A.G.
, Shubin Y.V.
, Shlyakhova E.V.
, Yudanov N.F.
, Pazhetnov E.M.
, Boronin A.I.
, Vyalikh D.V.
Effect of Fe/Ni Catalyst Composition on Nitrogen Doping and Field Emission Properties of Carbon Nanotubes
Carbon. 2008. V.46. N6. P.864-869. DOI: 10.1016/j.carbon.2008.02.009 WOS Scopus РИНЦ
Effect of Fe/Ni Catalyst Composition on Nitrogen Doping and Field Emission Properties of Carbon Nanotubes
Carbon. 2008. V.46. N6. P.864-869. DOI: 10.1016/j.carbon.2008.02.009 WOS Scopus РИНЦ
Даты:
Поступила в редакцию: | 31 июл. 2007 г. |
Принята к публикации: | 10 февр. 2008 г. |
Опубликована online: | 15 февр. 2008 г. |
Опубликована в печати: | 1 мая 2008 г. |
Идентификаторы БД:
Web of science | WOS:000256138000005 |
Scopus | 2-s2.0-43049103841 |
РИНЦ | 13585227 |
Chemical Abstracts | 2008:559811 |
Chemical Abstracts (print) | 149:453354 |
OpenAlex | W2012511354 |