Determination of the Type of Solid Solution of Nickel in Nickel Molybdate Научная публикация
Журнал |
Kinetics and Catalysis
ISSN: 0023-1584 , E-ISSN: 1608-3210 |
||
---|---|---|---|
Вых. Данные | Год: 1973, Том: 14, Номер: 5, Страницы: 1190-1191 Страниц : 2 | ||
Авторы |
|
||
Организации |
|
Реферат:
The formation of solid solution was observed in Ni-Mo oxide catalyst containing more Ni than the stoichiometric NiMoO4 compound. The Ni solubility region is within 1.1 to 1.20 Ni:Mo at. ratio. The catalyst samples prepared by coprecipitation of Ni(NO3)2 with NH4 paramolybdate (A., 1973) were heated at 480° prior to the x-ray diffraction study. At 1.10-1.20 Ni:Mo at. ratio the samples had the lowest d.
Библиографическая ссылка:
Plyasova L.M.
, Andrushkevich M.M.
, Buyanov R.A.
, Itenberg I.S.
Determination of the Type of Solid Solution of Nickel in Nickel Molybdate
Kinetics and Catalysis. 1973. V.14. N5. P.1190-1191. РИНЦ
Determination of the Type of Solid Solution of Nickel in Nickel Molybdate
Kinetics and Catalysis. 1973. V.14. N5. P.1190-1191. РИНЦ
Оригинальная:
Плясова Л.М.
, Андрушкевич М.М.
, Буянов Р.А.
, Итенберг И.Ш.
Определение типа твердого раствора никеля в молибдате никеля
Кинетика и катализ. 1973. Т.14. №5. С.1345-1346. РИНЦ
Определение типа твердого раствора никеля в молибдате никеля
Кинетика и катализ. 1973. Т.14. №5. С.1345-1346. РИНЦ
Идентификаторы БД:
РИНЦ | 29341447 |
Цитирование в БД:
БД | Цитирований |
---|---|
РИНЦ | 1 |