Synthesis of High Surface Area Zirconia Aerogels Using High Temperature Supercritical Drying Full article
Journal |
Nanostructured Materials
ISSN: 0965-9773 |
||||
---|---|---|---|---|---|
Output data | Year: 1997, Volume: 8, Number: 2, Pages: 119-135 Pages count : 17 DOI: 10.1016/S0965-9773(97)00011-1 | ||||
Tags | CATALYSTS; OXIDE; TRANSFORMATION; ADSORPTION; PARTICLES | ||||
Authors |
|
||||
Affiliations |
|
Funding (1)
1 | United States Department of the Army |
Abstract:
Zirconia aerogels were prepared by a sol-gel method followed by high temperature supercritical drying. Aerogels prepared in this way had surface areas up to 565 m2/ g after drying and above 100 m2/g after calcination at 500 °C for 2 hours. The calcined samples had symmetrical pore size distributions with average pore radii 70–170 Å and pore volumes 0.5–0.8 m3/g. Influence of preparation parameters such as precursor and solvent type, precursor and acid concentration, hydrolysis ratio, aging time, supercritical drying and subsequent calcination temperatures on the properties of the aerogels was studied systematically. Sol-gel preparation stabilized the tetragonal crystalline phase.
Cite:
Bedilo A.F.
, Klabunde K.J.
Synthesis of High Surface Area Zirconia Aerogels Using High Temperature Supercritical Drying
Nanostructured Materials. 1997. V.8. N2. P.119-135. DOI: 10.1016/S0965-9773(97)00011-1 WOS Scopus РИНЦ
Synthesis of High Surface Area Zirconia Aerogels Using High Temperature Supercritical Drying
Nanostructured Materials. 1997. V.8. N2. P.119-135. DOI: 10.1016/S0965-9773(97)00011-1 WOS Scopus РИНЦ
Dates:
Accepted: | Feb 5, 1997 |
Published print: | Mar 1, 1997 |
Published online: | May 19, 1998 |
Identifiers:
Web of science | WOS:A1997WT22300001 |
Scopus | 2-s2.0-0031096721 |
Elibrary | 13250725 |
Chemical Abstracts | 1997:269876 |
Chemical Abstracts (print) | 126:255854 |
OpenAlex | W2022368659 |