Complex Investigation of Porous Structure of Catalysts. 5. Ferric Hydroxide Oxide and Ferric-Oxide Научная публикация
Журнал |
Kinetics and Catalysis
ISSN: 0023-1584 , E-ISSN: 1608-3210 |
||
---|---|---|---|
Вых. Данные | Год: 1977, Том: 18, Номер: 6, Страницы: 1239-1246 Страниц : 8 | ||
Авторы |
|
||
Организации |
|
Реферат:
The origin of the pore structure in Fe2O3 and FeOOH catalysts formed during annealing at 150-800° was studied. Micropores are formed during the goethite-hematite transition at 250-350° due to the preservation of the hematite morphol. and the increase in the d. Further increases in temp. agglomerate the pores and reduce the porosity.
Библиографическая ссылка:
Dadayan K.A.
, Zagrafskaya R.V.
, Karnaukhov A.P.
, Fenelonov V.B.
Complex Investigation of Porous Structure of Catalysts. 5. Ferric Hydroxide Oxide and Ferric-Oxide
Kinetics and Catalysis. 1977. V.18. N6. P.1239-1246. WOS РИНЦ
Complex Investigation of Porous Structure of Catalysts. 5. Ferric Hydroxide Oxide and Ferric-Oxide
Kinetics and Catalysis. 1977. V.18. N6. P.1239-1246. WOS РИНЦ
Оригинальная:
Дадаян К.А.
, Заграфская Р.В.
, Карнаухов А.П.
, Фенелонов В.Б.
Комплексное исследование пористой структуры катализаторов. V. Гидроокись и окись железа
Кинетика и катализ. 1977. Т.18. №6. С.1517-1524. РИНЦ
Комплексное исследование пористой структуры катализаторов. V. Гидроокись и окись железа
Кинетика и катализ. 1977. Т.18. №6. С.1517-1524. РИНЦ
Идентификаторы БД:
Web of science | WOS:A1977FJ42100006 |
РИНЦ | 30628918 |
Цитирование в БД:
Пока нет цитирований