Synthesis of Highly Dispersed Zirconium Diboride for Fabrication of Special-Purpose Ceramic Научная публикация

Общее Язык: Английский, Жанр: Статья (Full article),
Статус опубликования: Опубликована, Оригинальность: Переводная
Журнал Russian Journal of Applied Chemistry
ISSN: 1070-4272 , E-ISSN: 1608-3296
Вых. Данные Год: 2017, Том: 90, Номер: 10, Страницы: 1579-1585 Страниц : 7 DOI: 10.1134/S1070427217100044
Авторы Krutskii Yu.L. 1 , Maksimovskii E.A. 2,3 , Popov M.V. 1 , Netskina O.V. 3,5 , Krutskaya T.M. 4 , Cherkasova N.Yu. 1 , Kvashina T.S. 1 , Drobyaz E.A. 1
Организации
1 Novosibirsk State Technical University, Novosibirsk, Russia
2 Institute of Inorganic Chemistry, Siberian Branch, Russian Academy of Sciences, Novosibirsk, Russia
3 Novosibirsk State University, Novosibirsk, Russia
4 Novosibirsk State Architectural-Constructional University, Novosibirsk, Russia
5 Boreskov Institute of Catalysis, Siberian Branch, Russian Academy of Sciences, Novosibirsk, Russia

Информация о финансировании (1)

1 Министерство образования и науки Российской Федерации СП-69.2016.1

Реферат: Reduction of zirconium dioxide with boron carbide and nanofibrous carbon in argon yielded a highly dispersed powder of zirconium diboride. Characteristics of zirconium diboride powders were examined by various analytical methods. The material obtained is represented by a single phase, zirconium diboride. Powder particles are for the most part aggregated. The average size of particles and aggregates is 10.9–12.9 μm with a wide size distribution. The specific surface area of the samples is 1.8–3.6 m2 g–1. The oxidation of zirconium diboride begins at a temperature of 640°C The optimal synthesis parameters were determined: ZrO2: B4C: C molar ratio of 2: 1: 3 (in accordance with stoichiometry), process temperature 1600–1700°C, synthesis duration 20 min.
Библиографическая ссылка: Krutskii Y.L. , Maksimovskii E.A. , Popov M.V. , Netskina O.V. , Krutskaya T.M. , Cherkasova N.Y. , Kvashina T.S. , Drobyaz E.A.
Synthesis of Highly Dispersed Zirconium Diboride for Fabrication of Special-Purpose Ceramic
Russian Journal of Applied Chemistry. 2017. V.90. N10. P.1579-1585. DOI: 10.1134/S1070427217100044 WOS Scopus РИНЦ
Оригинальная версия: Крутский Ю.Л. , Максимовский Е.А. , Попов М.В. , Нецкина О.В. , Крутская Т.М. , Черкасова Н.Ю. , Квашина Т.С. , Дробяз Е.А.
Синтез высокодисперсного диборида циркония для изготовления керамики специального назначения
Журнал прикладной химии. 2017. Т.90. №10. С.1295-1302. РИНЦ
Даты:
Опубликована в печати: 1 окт. 2017 г.
Поступила в редакцию: 18 окт. 2017 г.
Опубликована online: 5 февр. 2018 г.
Идентификаторы:
Web of science WOS:000425147900004
Scopus 2-s2.0-85042078053
РИНЦ 35488510
Chemical Abstracts 2018:301721
Альметрики: