Role of the Cu–Co Alloy and Cobalt Carbide in Higher Alcohol Synthesis Научная публикация
Конференция |
Physical Methods for Catalytic Research at the Molecular Level: International memorial K.I. Zamaraev conference 28 июн. - 2 июл. 1999 , Novosibirsk |
||
---|---|---|---|
Журнал |
Journal of Molecular Catalysis A: Chemical
ISSN: 1381-1169 |
||
Вых. Данные | Год: 2000, Том: 158, Номер: 1, Страницы: 389-393 Страниц : 5 DOI: 10.1016/S1381-1169(00)00110-2 | ||
Ключевые слова | Cobalt carbide, Cu-Co alloy, Cu-Co based catalyst, Higher alcohol synthesis, In situ XRD | ||
Авторы |
|
||
Организации |
|
Реферат:
Formation and decomposition of the Cu–Co alloy and Co2C were studied using in situ X-ray diffraction (XRD), TG-DTA and TEM techniques. Cu–Co alloy with ratio Cu/Co=1:1 has been obtained under treatment of CuCoO2 with hydrogen at 230–300°C. Co2C was formed from Cu–Co alloy at 280–310°C and decomposed at 390–400°C under CO. It was shown that the role of Cu–Co alloy consisted in formation of cobalt carbide was able to activate CO undissociatively that led to oxygenates synthesis.
Библиографическая ссылка:
Volkova G.G.
, Yurieva T.M.
, Plyasova L.M.
, Naumova M.I.
, Zaikovskii V.I.
Role of the Cu–Co Alloy and Cobalt Carbide in Higher Alcohol Synthesis
Journal of Molecular Catalysis A: Chemical. 2000. V.158. N1. P.389-393. DOI: 10.1016/S1381-1169(00)00110-2 WOS Scopus РИНЦ
Role of the Cu–Co Alloy and Cobalt Carbide in Higher Alcohol Synthesis
Journal of Molecular Catalysis A: Chemical. 2000. V.158. N1. P.389-393. DOI: 10.1016/S1381-1169(00)00110-2 WOS Scopus РИНЦ
Даты:
Опубликована online: | 18 июл. 2000 г. |
Опубликована в печати: | 8 сент. 2000 г. |
Идентификаторы БД:
Web of science | WOS:000089201200053 |
Scopus | 2-s2.0-0034622696 |
РИНЦ | 13347807 |
Chemical Abstracts | 2000:498714 |
Chemical Abstracts (print) | 133:336801 |
OpenAlex | W2026036367 |