Реферат: Mechanical activation (MA) combined with heat treatment at moderate temperatures was used to prepare disordered and highly dispersed LiCoO2 starting from the mixtures of various cobalt precursors (CoOOH, Co(OH)2, and Co) and LiOH. X-ray powder diffraction and IR spectroscopy were used to investigate the phase composition and the crystal structure of as-prepared samples, while the electronic state of cobalt ions was characterized by diffuse reflectance electron spectroscopy. MA of the LiOH+CoOOH mixture led to the formation of LT-LiCoO2 with a cubic spinel-related structure. Heat treatment at 600°C of the latter resulted in the formation of HT-LiCoO2 with a hexagonal layered structure similar to ceramic LiCoO2. However, as-prepared HT-LiCoO2 is characterized by Co3+O6 octahedra less perfect than those of ceramic LiCoO2. All MA-LiCoO2 samples are exclusively described by localized d electrons.

Библиографическая ссылка: Kosova N.V. , Anufrienko V.F. , Larina T.V. , Rougier A. , Aymard L. , Tarascon J.M.
Disordering and Electronic State of Cobalt Ions in Mechanochemically Synthesized LiCoO2
Journal of Solid State Chemistry. 2002. V.165. N1. P.56-64. DOI: 10.1006/jssc.2002.9493 WOS Scopus РИНЦ CAPlusCA OpenAlex

Даты:

Поступила в редакцию:	7 авг. 2001 г.
Принята к публикации:	21 дек. 2001 г.
Опубликована в печати:	1 апр. 2002 г.
Опубликована online:	25 мая 2002 г.

Идентификаторы БД:

Web of science:	WOS:000175169200009
Scopus:	2-s2.0-0036334599
РИНЦ:	13409598
Chemical Abstracts:	2002:303376
Chemical Abstracts (print):	137:225637
OpenAlex:	W2100701278

Цитирование в БД:

БД	Цитирований
Web of science	28
Scopus	31
OpenAlex	31

Альметрики: