Реферат: The phase compositions of α- and γ-alumina-supported manganese oxide catalysts (including X-ray amorphous phases) are found to depend on the calcination temperature. In all cases, highly defective phases are formed, whose structures are not completely identical to those of corresponding bulk oxides. It is shown that the reasons for the formation of such phases are Al3+ dissolution in manganese oxides, nonstoichiometry of the oxide composition, and the effect of stabilization of the interaction of manganese oxides with the support. The γ-Al2O3 to α-Al2O3 transition in the presence of supported manganese is proven to occur at lower temperatures than in the bulk systems. The highly defective β-Mn3O4 and β-Mn2O3 phases modified with Al3+ ions, which are formed in the course of thermal activation, are assumed to be active in catalytic complete oxidation.

Библиографическая ссылка: Kochubey D.I. , Kriventsov V.V. , Kustova G.N. , Odegova G.V. , Tsyrulʹnikov P.G. , Kudrya E.N.
Thermal Activation of a Post-Combustion Manganese-Alumina Catalyst Studied by IR, UV Spectroscopy, and EXAFS
Kinetics and Catalysis. 1998. V.39. N2. P.274-281. WOS Scopus РИНЦ CAPlusCA

Оригинальная: Кочубей Д.И. , Кривенцов В.В. , Кустова Г.Н. , Одегова Г.В. , Цырульников П.Г. , Кудря Е.Н.
Исследование термоактивации алюмомарганцевого катализатора дожигания методами ИК-, УФ-спектроскопии и EXAFS
Кинетика и катализ. 1998. Т.39. №2. С.294-301. РИНЦ

Даты:

Поступила в редакцию:

20 февр. 1997 г.

Идентификаторы БД:

Web of science:	WOS:000073168400018
Scopus:	2-s2.0-1542676978
РИНЦ:	13300459
Chemical Abstracts:	1998:265549
Chemical Abstracts (print):	128:285804

Цитирование в БД:

БД	Цитирований
Web of science	6