Mesoporous Composite Materials from Acivated Rice Husk Carbon and Montmorillonite Научная публикация

Журнал Eurasian Chemico-Technological Journal
ISSN: 1562-3920
Вых. Данные Год: 2011, Том: 13, Страницы: 105-111 Страниц : 7 DOI: 10.18321/ectj74
Авторы Jandosov J.M. 1 , Mansurov Z.A. 1 , BiIsenbayev M.A. 1 , Kerimkulova A.R. 1 , Ismagilov Z.R. 2 , Shikina N.V. 2 , Ismagilov I.Z. 2 , Andrievskaya I.P. 2
Организации
1 Institute of Combustion Problems, 172 Bogenbai Batyr st.,050012, Almaty, Kazakhstan
2 Boreskov Institute of Catalysis, 5, Pr.Akad.Lavrentieva, 630090, Novosibirsk, Russia

Реферат: Three different carbons were prepared from rice husk by steam activation at 700 ºC, H3PO4-activation followed by desilication or desilication followed by H3PO4-activation at 500ºC. Honeycomb monoliths were obtained by mixing of a carbon with montmorillonite followed by extrusion, curing, calcination and leaching by alkaline solution. Obtained blocks were compared in terms of their morphology and elemental composition using data of SEM/EDX-analysis. From low temperature nitrogen adsorption study results it follows that prepared monoliths are characterized by SBET up to 700 m2/g (VS = 0.79 cm3/g) and pore size distribution shows the maximum around 4 nm. Methylene blue number is as high as 250 mg/g.
Библиографическая ссылка: Jandosov J.M. , Mansurov Z.A. , BiIsenbayev M.A. , Kerimkulova A.R. , Ismagilov Z.R. , Shikina N.V. , Ismagilov I.Z. , Andrievskaya I.P.
Mesoporous Composite Materials from Acivated Rice Husk Carbon and Montmorillonite
Eurasian Chemico-Technological Journal. 2011. V.13. P.105-111. DOI: 10.18321/ectj74 Scopus РИНЦ CAPlusCA OpenAlex
Файлы: Полный текст от издателя
Даты:
Поступила в редакцию: 30 июн. 2010 г.
Опубликована online: 21 дек. 2010 г.
Идентификаторы БД:
Scopus: 2-s2.0-84865451682
РИНЦ: 20524781
Chemical Abstracts: 2012:228293
Chemical Abstracts (print): 157:555556
OpenAlex: W2201785699
Цитирование в БД:
БД Цитирований
Scopus 5
РИНЦ 5
OpenAlex 6
Альметрики: