Composite TiO2/Fiberglass Catalyst: Synthesis and Characterization Научная публикация

Журнал Catalysis Communications
ISSN: 1566-7367 , E-ISSN: 1873-3905
Вых. Данные Год: 2017, Том: 89, Страницы: 64-68 Страниц : 5 DOI: 10.1016/j.catcom.2016.10.018
Ключевые слова Anatase, Fiberglass catalyst, n-Heptane oxidation, Sol-gel synthesis, Titania
Авторы Shamsutdinova A.N. 1 , Brichkov A.S. 1 , Paukshtis E.A. 1,2,3 , Larina T.V. 2 , Cherepanova S.V. 2 , Glazneva T.S. 2,3 , Kozik V.V. 1
Организации
1 National Research Tomsk State University, Pr. Lenina, 36, Tomsk 634050, Russia
2 Boreskov Institute of Catalysis, Pr. Akademika Lavrentieva, 5, Novosibirsk 630090, Russia
3 Novosibirsk State University, Pirogova str., 2, Novosibirsk 630090, Russia

Информация о финансировании (1)

1 Министерство образования и науки Российской Федерации 11.801.2014/K

Реферат: The paper presents the synthesis and characterization of highly dispersed titania on the surface of fiberglass material. Scanning electron microscopy and X-ray digital 3D-microtomography showed that each support fiber was uniformly coated by modifying component. The layer of titania consisted of anatase particles of 18 nm, an average pore size was 3.1 nm. The prepared material revealed a catalytic activity in n-heptane cracking, deep and partial oxidation. The major products of n-heptane conversion at 300-400oC in the presence of oxygen were ketones with a carbon number of 3-4. Above 500oC, the deep oxidation increased dramatically with a simultaneous appearance of α-olefins.
Библиографическая ссылка: Shamsutdinova A.N. , Brichkov A.S. , Paukshtis E.A. , Larina T.V. , Cherepanova S.V. , Glazneva T.S. , Kozik V.V.
Composite TiO2/Fiberglass Catalyst: Synthesis and Characterization
Catalysis Communications. 2017. V.89. P.64-68. DOI: 10.1016/j.catcom.2016.10.018 WOS Scopus РИНЦ CAPlusCA OpenAlex
Даты:
Поступила в редакцию: 11 июл. 2016 г.
Принята к публикации: 23 окт. 2016 г.
Опубликована online: 26 окт. 2016 г.
Опубликована в печати: 1 янв. 2017 г.
Идентификаторы БД:
Web of science: WOS:000390511600015
Scopus: 2-s2.0-84993933919
РИНЦ: 28267764
Chemical Abstracts: 2016:1792112
Chemical Abstracts (print): 166:298814
OpenAlex: W2546143042
Цитирование в БД:
БД Цитирований
Web of science 11
Scopus 14
РИНЦ 24
OpenAlex 19
Альметрики: