Реферат: The properties of the pure alloys and those capsulated in alumina-containing matrices prepared by different methods were investigated. The catalysts with different Zr/Fe atomic ratio ∼2:1, 1:1 and 1:2 were prepared by alloying Zr and Fe at 2200-2400°C under Ar followed by hydrogenation of those alloys at a room temperature and hydrogen pressure of 5 MPa. The microtexture were characterized by using the nitrogen adsorption isotherms measured at 77 K on a ASAP-2400 Micromeritics instrument. It was observed that at higher temperatures AC is almost fully oxidized and decomposed in different iron enriched and Zr enriched components which leads to deactivation of AC.

Библиографическая ссылка: Tikhov S.F. , Kuzʹmin A.E. , Bespalko Y.N. , Kurkin V.I. , Sadykov V.A. , Bogolepova E.I. , Tsybulya S.V. , Kalinkin A.V. , Mordovin V.P. , Salanov A.N. , Zaikovskii V.I. , Shavorsky A.A.
ZrFe Intermetallides for FTS: Before and After Encapsulation in Alumina Containing Matrices
Preprints - American Chemical Society, Division of Petroleum Chemistry. 2005. V.50. P.188-191. Scopus РИНЦ CAPlusCA

Даты:

Опубликована в печати:

1 мар. 2005 г.

Идентификаторы БД:

Scopus:	2-s2.0-22744444307
РИНЦ:	13478211
Chemical Abstracts:	2005:213487
Chemical Abstracts (print):	143:213941

Цитирование в БД:

БД	Цитирований
Scopus	3
РИНЦ	3