Copper on Carbon Materials: Stabilization by Nitrogen Doping | Sciact - CRIS-система Института катализа

Copper on Carbon Materials: Stabilization by Nitrogen Doping Научная публикация

Журнал

Journal of Materials Chemistry A, Materials for Energy and Sustainability
ISSN: 2050-7488 , E-ISSN: 2050-7496

Вых. Данные

Год: 2017, Том: 5, Номер: 21, Страницы: 10574-10583 Страниц : 10 DOI: 10.1039/c7ta02282d

Ключевые слова

FORMIC-ACID DECOMPOSITION; X-RAY PHOTOELECTRON; N-DOPED CARBON; HYDROGEN-PRODUCTION; CU CATALYSTS; NANOPARTICLES; REDUCTION; NICKEL; NANOFIBERS; PARTICLES

Авторы

Bulushev Dmitri A. ^1,2,3 , Chuvilin Andrey L. ^4,5 , Sobolev Vladimir I. ^1,2 , Stolyarova Svetlana G. ² , Shubin Yury V. ^2,3 , Asanov Igor P. ^2,3 , Ishchenko Arcady V. ^1,3 , Magnani Giacomo ⁶ , Riccò Mauro ⁶ , Okotrub Alexander V. ^2,3 , Bulusheva Lyubov G. ^2,3

Организации

1	Boreskov Institute of Catalysis, SB RAS, Novosibirsk, 630090, Russia
2	Nikolaev Institute of Inorganic Chemistry, SB RAS, Novosibirsk, 630090, Russia
3	Novosibirsk State University, Novosibirsk, 630090, Russia
4	CIC nanoGUNE Consolider, San Sebastian, 20018, Spain
5	IKERBASQUE, Basque Foundation for Science, Bilbao, 20013, Spain
6	Dipartimento di Scienze Matematiche, Fisiche e Informatiche, Universita di Parma, ` 43124 Parma, Italy

Информация о финансировании (1)

Российский научный фонд

16-13-00016

The applicability of Cu/C catalysts is limited by sintering of Cu leading to deactivation in catalytic reactions. We show that the problem of sintering could be resolved by N-doping of the carbon support. Cu nanocatalysts with 1 at% of metal were synthesized by Cu acetate decomposition on N-free and N-doped (5.7 at% N) mesoporous carbon supports as well as on thermally expanded graphite oxide. Catalytic properties of these samples were compared in hydrogen production from formic acid decomposition. The N-doping leads to a strong interaction of the Cu species with the support providing stabilization of Cu in the form of clusters of less than 5 nm in size and single Cu atoms, which were observed in a significant ratio by atomic resolution HAADF/STEM even after testing the catalyst under harsh conditions of the reaction at 600 K. The mean size of the obtained Cu clusters was by a factor of 7 smaller than that of the particles in the N-free catalyst. The N-doped Cu catalyst possessed good stability in the formic acid decomposition at 478 K for at least 7 h on-stream and a significantly higher catalytic activity than the N-free Cu catalysts. The nature of the strongly interacting Cu species was studied by XPS, XRD and other methods as well as by DFT calculations. The presence of single Cu atoms in the N-doped catalysts should be attributed to their strong coordination by pyridinic nitrogen atoms at the edge of the graphene sheets of the support. We believe that the N-doping of the carbon support will allow expanding the use of Cu/C materials for different applications avoiding sintering and deactivation.

Bulushev D.A. , Chuvilin A.L. , Sobolev V.I. , Stolyarova S.G. , Shubin Y.V. , Asanov I.P. , Ishchenko A.V. , Magnani G. , Riccò M. , Okotrub A.V. , Bulusheva L.G.
Copper on Carbon Materials: Stabilization by Nitrogen Doping

Journal of Materials Chemistry A, Materials for Energy and Sustainability. 2017. V.5. N21. P.10574-10583. DOI: 10.1039/c7ta02282d WOS Scopus РИНЦ CAPlusCA OpenAlex

Полный текст от издателя

Поступила в редакцию:	15 мар. 2017 г.
Принята к публикации:	25 апр. 2017 г.
Опубликована online:	26 апр. 2017 г.
Опубликована в печати:	7 июн. 2017 г.

Web of science:	WOS:000402387900055
Scopus:	2-s2.0-85021627317
РИНЦ:	31045301
Chemical Abstracts:	2017:671999
Chemical Abstracts (print):	167:252462
OpenAlex:	W2609911228

БД	Цитирований
Web of science	117
Scopus	120
РИНЦ	113
OpenAlex	126