Silicate Fiberglasses Modified with Quaternary Ammonium Base for Natural Gas Desulfurization Научная публикация

Журнал Industrial and Engineering Chemistry Research
ISSN: 0888-5885 , E-ISSN: 1520-5045
Вых. Данные Год: 2017, Том: 56, Номер: 37, Страницы: 10318-10328 Страниц : 11 DOI: 10.1021/acs.iecr.7b01389
Ключевые слова AdsorptionDesorptionElectron microscopyFourier transform infrared spectroscopyGlass fibersHigh resolution transmission electron microscopyMagic angle spinningScanning electron microscopySilicatesSulfur determinationTransmission electron microscopy
Авторы Bal’zhinimaev Bair S. 1 , Kovalyov Evgenii V. 1 , Suknev Alexei P. 1 , Paukshtis Eugenii A. 1,2 , Khabibulin Dzhalil F. 1,2 , Batueva Irina S. 3 , Salanov Aleksey N. 1 , Riley Mark G. 4
Организации
1 Boreskov Institute of Catalysis, Prospekt Ak. Lavrentieva 5, Novosibirsk, 630090, Russia
2 Novosibirsk State University, Pirogova St. 1, Novosibirsk, 630090, Russia
3 Buryat State University, Smolina St. 24a, Ulan-Ude, 670000, Russia
4 Honeywell UOP, 25 E. Algonquin Road, Des Plaines, Illinois 60017, United States

Информация о финансировании (2)

1 Федеральное агентство научных организаций России 0303-2016-0006 (V.44.1.6)
2 Honeywell UOP (formely UOP LLC) 15C0882

Реферат: A new gel-like film was generated on the surface of silicate fiberglass (FG) under hydrothermal treatment with tetramethylammonium hydroxide (TMAH) water solution. By means of scanning electron microscopy (SEM)/high resolution transmission electron microscopy (HRTEM), 1H NMR magic angle spinning (MAS), and diffuse reflectance infrared fourier transform spectroscopy (DRIFTS), we revealed this film is a phase with density less than pristine FG, where TMA species, as the H2S adsorption sites, are confined. Indeed, FGs modified in this way exhibited a rather high dynamic adsorption capacity which was proportional to concentration of TMA cations bonded with very basic oxygen of Broensted acid residue. The N-modified FG sorbents showed good regenerability when in the presence of water, and the adsorbed hydrogen sulfide on the TMA+––O–Si ion pair was easily desorbed at room temperature. This gives grounds to conclude that the process of hydrogen sulfide sorption on N-modified FGs is reversible and proceeds without a loss of adsorption capacity. Indeed, N-modified FGs remained stable during several adsorption–desorption cycles.
Библиографическая ссылка: Bal’zhinimaev B.S. , Kovalyov E.V. , Suknev A.P. , Paukshtis E.A. , Khabibulin D.F. , Batueva I.S. , Salanov A.N. , Riley M.G.
Silicate Fiberglasses Modified with Quaternary Ammonium Base for Natural Gas Desulfurization
Industrial and Engineering Chemistry Research. 2017. V.56. N37. P.10318-10328. DOI: 10.1021/acs.iecr.7b01389 WOS Scopus РИНЦ CAPlus OpenAlex
Даты:
Поступила в редакцию: 4 апр. 2017 г.
Принята к публикации: 21 авг. 2017 г.
Опубликована online: 6 сент. 2017 г.
Опубликована в печати: 20 сент. 2017 г.
Идентификаторы БД:
Web of science: WOS:000411659400011
Scopus: 2-s2.0-85029767774
РИНЦ: 31071322
Chemical Abstracts: 2017:1439741
OpenAlex: W2750639565
Цитирование в БД:
БД Цитирований
Web of science 3
Scopus 3
РИНЦ 4
OpenAlex 4
Альметрики: