Реферат: New results on the preparation of palladium fiberglass catalysts, their characterization by means of XPS, STEM and HS-LEIS, as well as kinetic and mechanistic data on selective hydrogenation of acetylene followed from SSITKA are presented. The effective ways of confining 1 nm Pd clusters in the subsurface layers of glass and increasing their concentration were developed. Namely, these small clusters were shown to be responsible for high catalyst performance. The SSITKA study using 13C labeled acetylene clearly demonstrated that gas-phase ethylene was not involved in the reaction even at its very high excess. This fact was explained by the ability of glass to absorb predominantly such readily polarizable molecules like acetylene, but not ethylene. As a result, at a complete acetylene conversion our single-component Pd/FG catalyst demonstrates high selectivity (the ethylene increment of 60 %), which is higher than that of commercial bimetallic one.

Библиографическая ссылка: Gulyaeva Y.K. , Kaichev V.V. , Zaikovskii V.I. , Suknev A.P. , Brongersma H.H. , Balʹzhinimaev B.S.
Selective Hydrogenation Processes over Novel Fiberglass Based Catalysts
В сборнике EuropaCat XII. Catalysis: Balancing the use of fossil and renewable resources. XII European Congress on Catalysis, Kazan (Russia), 30 August - 4 September, 2015 : Book of Abstracts. – BIC SB RAS., 2015. – C.335-336. – ISBN 978-5-906376-10-7.

Идентификаторы БД: Нет идентификаторов

Цитирование в БД: Пока нет цитирований