Study on Thermal Stability of Ceria-Supported Rhodium Catalysts Научная публикация

Конференция 7th International Conference on Material Science and Engineering Technology
20-22 окт. 2018 , Beijing
Сборник Material Science and Engineering Technology VII : 7th International Conference on Material Science and Engineering Technology (ICMSET 2018)
Сборник, Trans Tech Publications Ltd. Zurich, Switzerland.2019. 220 c. ISBN 9783035715392.
Журнал Materials Science Forum
ISSN: 0255-5476 , E-ISSN: 1662-9752
Вых. Данные Год: 2019, Том: 950, Страницы: 190-194 Страниц : 5 DOI: 10.4028/www.scientific.net/MSF.950.190
Ключевые слова Cerium oxide; rhodium; textural properties; CO oxidation; thermal stability
Авторы Kenzhin Roman M. 1 , Alikin Evgeny A. 2 , Denisov Sergey P. 2 , Vedyagin Aleksey A. 1,3
Организации
1 Boreskov Institute of Catalysis SB RAS, pr. Ac. Lavrentieva, 5, Novosibirsk, 630090, Russia
2 Ecoalliance Ltd, Dzerzhinskogo str., 2, Novouralsk, 624131 Russia
3 National Research Tomsk Polytechnic University, Lenin av., 30, Tomsk, 634050, Russia

Информация о финансировании (2)

1 Федеральное агентство научных организаций России 0303-2016-0002
2 Министерство образования и науки Российской Федерации 4.5200.2017

Реферат: In the present work, the impact of the rhodium deposition on the thermal stability of ceria-based catalysts was studied. The samples were prepared by an incipient wetness impregnation of the support with aqueous solution of rhodium nitrate. The loading of Rh was 0.1 and 1 wt.%. The textural characteristics of the samples were examined by a low-temperature nitrogen adsorption. It was shown that the addition of rhodium intensifies the process of ceria agglomeration, which leads to the lower values of specific surface area along with increased average pore diameter after the aging at 1000 °C. Stability of the catalysts was investigated by means of a prompt thermal aging procedure. The high-loaded catalyst (1 wt.% Rh/CeO2) was more active than the 0.1 wt.% Rh/CeO2 sample, while the stability of both the catalysts was excellent. It should be emphasized that the alumina-based reference samples with the similar rhodium loading were significantly less active and poorly stable.
Библиографическая ссылка: Kenzhin R.M. , Alikin E.A. , Denisov S.P. , Vedyagin A.A.
Study on Thermal Stability of Ceria-Supported Rhodium Catalysts
В сборнике Material Science and Engineering Technology VII : 7th International Conference on Material Science and Engineering Technology (ICMSET 2018). – Trans Tech Publications Ltd., 2019. – C.190-194. – ISBN 9783035715392. DOI: 10.4028/www.scientific.net/MSF.950.190 Scopus РИНЦ OpenAlex
Даты:
Поступила в редакцию: 26 окт. 2018 г.
Принята к публикации: 1 нояб. 2018 г.
Опубликована online: 3 апр. 2019 г.
Идентификаторы БД:
Scopus: 2-s2.0-85066628013
РИНЦ: 41624533
OpenAlex: W2925820624
Цитирование в БД:
БД Цитирований
Scopus 6
РИНЦ 5
OpenAlex 5
Альметрики: