Particularities of Low-Temperature WGSR over Ceramometal and Oxide Catalysts: Effect of Catalyst Particle Size Научная публикация

Журнал Chemical Engineering Journal
ISSN: 1385-8947 , E-ISSN: 1873-3212
Вых. Данные Год: 2019, Том: 374, Страницы: 405-411 Страниц : 7 DOI: 10.1016/j.cej.2019.05.089
Ключевые слова Effectiveness factor; Oxide and ceramometal catalysts; WGS reaction
Авторы Tikhov S.F. 1 , Minyukova T.P. 1 , Reshetnikov S.I. 1 , Valeev K.R. 1 , Vernikovskaya N.V. 1 , Salanov A.N. 1 , Cherepanova S.V. 1 , Sadykov V.A. 1
Организации
1 Boreskov Institute of Catalysis SB RAS, Novosibirsk, Russian Federation

Информация о финансировании (1)

1 Федеральное агентство научных организаций России 0303-2016-0013

Реферат: Two types of the low temperature WGS catalysts were compared: oxide Cu-Zn-Al catalyst prepared through coprecipitation procedure and ceramometal CuAlO/CuA catalyst prepared from powdered CuAl alloy. The catalysts were characterized by XRD, SEM with EDX, adsorption-desorption isotherms. Activity was measured at a pressure of 1 bar in the mixture of CO:Н2О:Н2 = 8:42:50 at a steam/gas ratio of 0.6–0.7. The catalysts were used as a small (0.14–0.25 mm) and large (3.2 × 3.2 × 5 mm) fraction. It was found that oxide catalyst possesses of a developed mesopore structure with specific surface area 122 m2/g while ceramometal catalyst has a developed macropore structure with size up to ten microns and specific surface area 15.7 m2/g. As a result, large fraction (granules)of ceramometal catalyst has twofold higher effectiveness factor due to higher internal diffusion. © 2019
Библиографическая ссылка: Tikhov S.F. , Minyukova T.P. , Reshetnikov S.I. , Valeev K.R. , Vernikovskaya N.V. , Salanov A.N. , Cherepanova S.V. , Sadykov V.A.
Particularities of Low-Temperature WGSR over Ceramometal and Oxide Catalysts: Effect of Catalyst Particle Size
Chemical Engineering Journal. 2019. V.374. P.405-411. DOI: 10.1016/j.cej.2019.05.089 WOS Scopus РИНЦ OpenAlex
Даты:
Опубликована online: 16 мая 2019 г.
Опубликована в печати: 15 окт. 2019 г.
Идентификаторы БД:
Web of science: WOS:000477652900038
Scopus: 2-s2.0-85066295528
РИНЦ: 41636905
OpenAlex: W2944838526
Цитирование в БД:
БД Цитирований
Scopus 8
Web of science 8
РИНЦ 10
OpenAlex 9
Альметрики: