Oxidation and Recrystallization of Platinum Group Metals (Pt, Pd, Rh) in Oxygen. Surface and Subsurface Reconstruction of Polycrystalline Platinum During Annealing in the O2 Atmosphere over the Temperature Range of 600–1400 K Научная публикация
| Журнал |
Applied Surface Science
ISSN: 0169-4332 |
||
|---|---|---|---|
| Вых. Данные | Год: 2019, Том: 490, Страницы: 188-203 Страниц : 16 DOI: 10.1016/j.apsusc.2019.05.289 | ||
| Ключевые слова | Scanning electron microscopy; Polycrystalline platinum; Oxygen; Metal oxidation; Recrystallization | ||
| Авторы |
|
||
| Организации |
|
Информация о финансировании (1)
| 1 | Федеральное агентство научных организаций России | 0303-2016-0002 |
Реферат:
Scanning electron microscopy, energy-dispersive and X-ray photoelectron spectroscopies, as well as X-ray diffraction analysis were used to study the morphology, microstructure and chemical composition of surface and
subsurface layers of Pt(poly) after treatment in O2 at T = 600–1400 K. It was found that the Pt(poly) microstructure is determined by the reaction of O2 with the surface carbon and platinum recrystallization. At
T = 600–1000 K a part of the surface graphite-like film is removed and the surface microstructure remains
virtually unchanged. The fcc lattice parameter of platinum (a), the size of the coherent scattering region (D), and
microdistortion of the metal lattice (ε) virtually do not change and are equal to 3.920 Å, 100 nm and 0.05%,
respectively. At T > 1000 K, the а value remains virtually constant and sizes of D, grains and microfacets
substantially increase to ca. 500–600 nm, 40 and 1 μm, whereas the ε value decreases to ca. 0.014%. At
T = 600–1400 K, dissolution of oxygen in the platinum lattice and formation of bulk PtO2 oxide are not observed; however, oxygen is able to accumulate at grain boundaries and other defects in the amount of 5–10 at.%.
Библиографическая ссылка:
Salanov A.N.
, Kochurova N.M.
, Serkova A.N.
, Kalinkin A.V.
, Isupova L.A.
, Parmon V.N.
Oxidation and Recrystallization of Platinum Group Metals (Pt, Pd, Rh) in Oxygen. Surface and Subsurface Reconstruction of Polycrystalline Platinum During Annealing in the O2 Atmosphere over the Temperature Range of 600–1400 K
Applied Surface Science. 2019. V.490. P.188-203. DOI: 10.1016/j.apsusc.2019.05.289 WOS Scopus РИНЦ CAPlusCA OpenAlex
Oxidation and Recrystallization of Platinum Group Metals (Pt, Pd, Rh) in Oxygen. Surface and Subsurface Reconstruction of Polycrystalline Platinum During Annealing in the O2 Atmosphere over the Temperature Range of 600–1400 K
Applied Surface Science. 2019. V.490. P.188-203. DOI: 10.1016/j.apsusc.2019.05.289 WOS Scopus РИНЦ CAPlusCA OpenAlex
Даты:
| Поступила в редакцию: | 1 мар. 2019 г. |
| Принята к публикации: | 24 мая 2019 г. |
| Опубликована online: | 4 июн. 2019 г. |
| Опубликована в печати: | 1 окт. 2019 г. |
Идентификаторы БД:
| Web of science: | WOS:000472709100022 |
| Scopus: | 2-s2.0-85067807661 |
| РИНЦ: | 41650856 |
| Chemical Abstracts: | 2019:1181582 |
| Chemical Abstracts (print): | 171:183625 |
| OpenAlex: | W2948759278 |