Intermediate Temperature Proton Electrolytes Based on Cesium Dihydrogen Phosphate and Butvar Polymer Научная публикация
| Журнал |
Ionics
ISSN: 0947-7047 , E-ISSN: 1862-0760 |
||||
|---|---|---|---|---|---|
| Вых. Данные | Год: 2020, Том: 26, Номер: 4, Страницы: 1813-1818 Страниц : 6 DOI: 10.1007/s11581-020-03505-9 | ||||
| Ключевые слова | Proton conductivity . Acid salt . Cesium dihydrogen phosphate . Polyvinyl butyral . Composite polymer electrolyte | ||||
| Авторы |
|
||||
| Организации |
|
Реферат:
The phase composition, electrotransport properties, and spectral characteristics of the (1 − x)CsH2PO4–xButvar system (х = 0–0.2 wt%) were investigated in details. Butvar was proved to be a chemically suitable matrix for CsH2PO4 with a good adhesion to acid salt permitting the formation of flexible membrane. The chemical interaction of organic matrix with acid salt was not observed. A new method of “polymer-CsH2PO4” composites preparation through alcohol solutions of initial components was proposed. The flexible and thin (~ 200 μm) proton membranes with uniform salt distribution were obtained. Composite polymer electrolytes are characterized by high proton conductivity values (~ 5 × 10−3 S/cm) at 240 °C and are stable under conditions of high humidity (PH2O ~ 0.3 atm.).
Библиографическая ссылка:
Bagryantseva I.N.
, Gaydamaka A.A.
, Ponomareva V.G.
Intermediate Temperature Proton Electrolytes Based on Cesium Dihydrogen Phosphate and Butvar Polymer
Ionics. 2020. V.26. N4. P.1813-1818. DOI: 10.1007/s11581-020-03505-9 WOS Scopus РИНЦ CAPlusCA OpenAlex
Intermediate Temperature Proton Electrolytes Based on Cesium Dihydrogen Phosphate and Butvar Polymer
Ionics. 2020. V.26. N4. P.1813-1818. DOI: 10.1007/s11581-020-03505-9 WOS Scopus РИНЦ CAPlusCA OpenAlex
Даты:
| Поступила в редакцию: | 8 окт. 2019 г. |
| Принята к публикации: | 20 февр. 2020 г. |
| Опубликована online: | 7 мар. 2020 г. |
| Опубликована в печати: | 1 апр. 2020 г. |
Идентификаторы БД:
| Web of science: | WOS:000521777200025 |
| Scopus: | 2-s2.0-85081662437 |
| РИНЦ: | 43251379 |
| Chemical Abstracts: | 2020:463776 |
| Chemical Abstracts (print): | 173:921398 |
| OpenAlex: | W3010138592 |