Iron Induced Porosity of the Templated Carbon for Enhancement of Electrochemical Capacitance Full article

Journal

Applied Surface Science
ISSN: 0169-4332

Output data

Year: 2021, Volume: 543, Article number : 148565, Pages count : 14 DOI: 10.1016/j.apsusc.2020.148565

Tags

Templated carbon; Calcium tartrate; Iron-doping; Pore structure; CVD synthesis; Electrical double-layer capacitor

Authors

Shlyakhova Elena V. ¹ , Okotrub Alexander V. ¹ , Fedoseeva Yuliya V. ¹ , Fedorovskaya Ekaterina O. ¹ , Mel'gunova Elena A. ² , Mel'gunov Maxim S. ² , Koroteev Victor O. ¹ , Makarova Anna A. ³ , Zhou Jisheng ⁴ , Song Huaihe ⁴ , Bulusheva Lyubov G. ¹

Affiliations

1	Nikolaev Institute of Inorganic Chemistry, SB RAS, 3 Acad. Lavrentiev Ave., 630090 Novosibirsk, Russia
2	Boreskov Institute of Catalysis, SB RAS, 5 Acad. Lavrentiev Ave., 630090 Novosibirsk, Russia
3	Physical Chemistry, Institute of Chemistry and Biochemistry, Free University of Berlin, 14195 Berlin, Germany
4	State Key Laboratory of Chemical Resource Engineering, Beijing University of Chemical Technology, 100029 Beijing, PR China

Funding (1)

Russian Science Foundation

19-73-10068 (АААА-А19-119070590004-6)

Porous carbon (PC) materials with a large specific surface area and high volume of mesopores were produced using iron-doped calcium tartrate (CaTr) as a template precursor and ethanol as a carbon source. The iron doping concentration was varied from 0.2 to 1.6 at%. Template precursor was decomposed in argon at 800 °C, the formed template nanoparticles were immediately used for chemical vapor deposition (CVD) of ethanol, and after the synthesis, they were removed by HCl treatment. It was shown that the template consisted of CaO nanoparticles 5–20 nm in size with oxidized carbon layers on the surface. The incorporation of iron into CaTr promoted graphitization of the carbon layers and led to formation of iron oxide nanoparticles 3–4 nm in size. These nanoparticles served as a replica for small mesopores in the graphitic layers obtained in the ethanol CVD process. PC materials grown on the templates with an iron doping 0.2–0.4 at% were enriched with small mesopores, and due to this, they had a surface area of 907–931 m2 g−1 and pore volume of 3.3 cm3 g−1. These materials showed the highest specific capacitances of 280–230 F g−1 at 2 mV s−1 in 1 M H2SO4 electrolyte and a good rate capability.

Shlyakhova E.V. , Okotrub A.V. , Fedoseeva Y.V. , Fedorovskaya E.O. , Mel'gunova E.A. , Mel'gunov M.S. , Koroteev V.O. , Makarova A.A. , Zhou J. , Song H. , Bulusheva L.G.
Iron Induced Porosity of the Templated Carbon for Enhancement of Electrochemical Capacitance
Applied Surface Science. 2021. V.543. 148565 :1-14. DOI: 10.1016/j.apsusc.2020.148565 WOS Scopus РИНЦ AN OpenAlex

Submitted:	Aug 8, 2020
Accepted:	Nov 19, 2020
Published online:	Dec 26, 2020
Published print:	Mar 30, 2021

Web of science:	WOS:000613941800001
Scopus:	2-s2.0-85098704736
Elibrary:	45037746
Chemical Abstracts:	2021:25293
OpenAlex:	W3117683222

DB	Citing
Scopus	4
Web of science	4
Elibrary	5
OpenAlex	4