Реферат: The valence states and local structure around Mn atoms in mixed-valence Mn2BO4 have been studied by temperature dependent X-ray powder diffraction (XRPD), X-ray photoelectron (XPS) and Mn K-edge X-ray absorption (XAFS) spectroscopies measurements. X-ray absorption near-edge structure (XANES) and XPS have been used to measure the average oxidation state of Mn in bulk and near-surface of the material. The edge position, peak shapes and pre-edge features of Mn K-edge XANES spectra have been discussed. The pronounced temperature dependence of the Debye-Waller (DW) factor corresponding to the Mn-O coordination shell has been found from the extended x-ray absorption fine structure (EXAFS) analysis and has been associated with variations in the local distortions in MnO6 octahedra and emergence of short-range magnetic correlations at low temperatures. The XRPD measurements have been carried out at 298, 523 and 773 K. The monoclinic symmetry (P2(1)/n) was found to persist up to highest temperature measured. The BVS calculations have revealed large valence difference between two manganese sites that strongly supports the presence of charge ordering up to high temperatures.

Библиографическая ссылка: Kazak N.V. , Platunov M.S. , Knyazev Y.V. , Moshkina E.M. , Solovyov L.A. , Vereshchagin S.N. , Mikhlin Y.L. , Veligzhanin A.A. , Trigub A.L. , Ovchinnikov S.G.
Study of Mixed-Valence Mn2BO4 Using XRD, XPS and XAFS Spectroscopies
Physica B: Condensed Matter. 2019. V.560. P.228-235. DOI: 10.1016/j.physb.2019.02.019 WOS Scopus РИНЦ CAPlusCA OpenAlex

Даты:

Поступила в редакцию:	5 окт. 2018 г.
Принята к публикации:	12 февр. 2019 г.
Опубликована online:	15 февр. 2019 г.
Опубликована в печати:	1 мая 2019 г.

Идентификаторы БД:

Web of science:	WOS:000460635900034
Scopus:	2-s2.0-85062060247
РИНЦ:	41788980
Chemical Abstracts:	2019:391048
Chemical Abstracts (print):	173:75271
OpenAlex:	W2911407015

Цитирование в БД:

БД	Цитирований
Web of science	8
Scopus	9
OpenAlex	12

Альметрики: