Structured Composite Catalyst Pd/Ce0.75Zr0.25O2-x/θ-Al2O3/FeCrAlloy for Complete Oxidation of Methane Научная публикация

Журнал Materials Letters
ISSN: 0167-577X , E-ISSN: 1873-4979
Вых. Данные Год: 2022, Том: 310, Номер статьи : 131481, Страниц : 4 DOI: 10.1016/j.matlet.2021.131481
Ключевые слова Alumina; FeCr Alloy wire mesh; Structured catalysts; Ce-Zr mixed oxide; Preparation
Авторы Rogozhnikov V.N. 1,2 , Salanov A.N. 2 , Potemkin D.I. 3,4 , Pakharukova V.P. 2,4 , Stonkus O.A. 2 , Glotov A.P. 1 , Boev S.S. 1 , Zasypalov G.O. 1 , Melnikov D.P. 1 , Snytnikov P.V. 2
Организации
1 Gubkin Russian State University of Oil and Gas, Pr. Leninsky, 65, Moscow 119991, Russia
2 Boreskov Institute of Catalysis, Pr. Lavrentieva, 5, Novosibirsk 630090, Russia
3 Novosibirsk State Technical University, Karl Marx Pr., 20, Novosibirsk 630073, Russia
4 Novosibirsk State University, Pirogova st., 2, Novosibirsk 630090, Russia

Информация о финансировании (2)

1 Российский фонд фундаментальных исследований 19-33-60057 (АААА-А20-120020490072-7)
2 Российский научный фонд 21-73-20075

Реферат: Structured catalyst Pd/Ce0.75Zr0.25O2-x/Al2O3/FeCrAl was prepared via multistep solution synthesis. The prepared catalyst was characterized by X-Ray diffraction analysis (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), the specific surface area was measured by N2 adsorption (BET). The catalyst was tested in the deep oxidation of methane at excess air ratio ranging from 1.05 to 2. During the tests, the catalyst ensured complete methane conversion and zero CO content in the exhaust gases.
Библиографическая ссылка: Rogozhnikov V.N. , Salanov A.N. , Potemkin D.I. , Pakharukova V.P. , Stonkus O.A. , Glotov A.P. , Boev S.S. , Zasypalov G.O. , Melnikov D.P. , Snytnikov P.V.
Structured Composite Catalyst Pd/Ce0.75Zr0.25O2-x/θ-Al2O3/FeCrAlloy for Complete Oxidation of Methane
Materials Letters. 2022. V.310. 131481 :1-4. DOI: 10.1016/j.matlet.2021.131481 WOS Scopus РИНЦ CAPlus OpenAlex
Даты:
Поступила в редакцию: 31 авг. 2021 г.
Принята к публикации: 8 дек. 2021 г.
Опубликована online: 13 дек. 2021 г.
Опубликована в печати: 1 мар. 2022 г.
Идентификаторы БД:
Web of science: WOS:000736658300002
Scopus: 2-s2.0-85122426920
РИНЦ: 47920219
Chemical Abstracts: 2021:2830996
OpenAlex: W4200303426
Цитирование в БД:
БД Цитирований
Web of science 6
Scopus 6
РИНЦ 5
OpenAlex 6
Альметрики: