(Cd,Mn)S in the Composite Photocatalyst: Zinc Blende and Wurtzite Particles or Integrowth of These Two Modifications? Научная публикация
| Журнал |
Materials
ISSN: 1996-1944 |
||
|---|---|---|---|
| Вых. Данные | Год: 2023, Том: 16, Номер: 2, Номер статьи : 692, Страниц : 13 DOI: 10.3390/ma16020692 | ||
| Ключевые слова | cadmium-manganese sulfide; X-ray diffraction; disordered structure; stacking faults; anisotropic particle shape | ||
| Авторы |
|
||
| Организации |
|
Информация о финансировании (1)
| 1 | Министерство науки и высшего образования Российской Федерации (с 15 мая 2018) | 0239-2021-0003 |
Реферат:
In this study, the crystalline structure and particle shape of Cd1−xMnxS (x~0.3) in the composite photocatalysts prepared by hydrothermal synthesis at different temperatures (T = 80, 100, 120, and 140 °C) were analyzed. Along with mixed Cd–Mn sulfide, the catalysts contain a small amount of β-Mn3O4. XRD patterns of (Cd,Mn)S have features inherent to both cubic zinc blende and hexagonal wurtzite structure. Moreover, XRD peaks are anisotropically broadened. First, the heterogeneous (or two-phased) model was considered by the commonly used Rietveld method. Phase ratio, average crystallite sizes, and strains for both phases were formally determined. However, it was shown that this model is not correct because relatively narrow and broad peaks cannot be fitted simultaneously. Then, the homogeneous model was tested by Debye Function Analysis. This model assumes that particles are statistically homogeneous, but each particle contains lamellar intergrowth of zinc blende and wurtzite modifications. The probability of stacking faults, as well as the average radii of spherical and ellipsoidal particles, were varied. It was shown that nanocrystalline Cd0.7Mn0.3S particles have an ellipsoidal shape. Ellipsoids are elongated along the direction normal to the plane of defects. An increase in the hydrothermal synthesis temperature from 80°C to 140°C leads to an enlargement of particles and a gradual decrease in the probability of stacking faults in the wurtzite structure from 0.47 to 0.36. Therefore, with increasing temperature, the structure of (Cd,Mn)S nanoparticles transforms from almost random polytype cubic/hexagonal (ZB:WZ = 47:53) to a preferably hexagonal structure
(ZB:WZ = 36:64). Mn2+ ions facilitate CdS phase transformation from zinc blende to wurtzite structure. There is no direct correlation between the structure and photocatalytic activity.
Библиографическая ссылка:
Cherepanova S.
, Kozlova E.
(Cd,Mn)S in the Composite Photocatalyst: Zinc Blende and Wurtzite Particles or Integrowth of These Two Modifications?
Materials. 2023. V.16. N2. 692 :1-13. DOI: 10.3390/ma16020692 WOS Scopus РИНЦ CAPlus PMID OpenAlex
(Cd,Mn)S in the Composite Photocatalyst: Zinc Blende and Wurtzite Particles or Integrowth of These Two Modifications?
Materials. 2023. V.16. N2. 692 :1-13. DOI: 10.3390/ma16020692 WOS Scopus РИНЦ CAPlus PMID OpenAlex
Даты:
| Поступила в редакцию: | 19 нояб. 2022 г. |
| Принята к публикации: | 8 янв. 2023 г. |
| Опубликована в печати: | 10 янв. 2023 г. |
| Опубликована online: | 10 янв. 2023 г. |
Идентификаторы БД:
| Web of science: | WOS:000916399200001 |
| Scopus: | 2-s2.0-85146599323 |
| РИНЦ: | 54007669 |
| Chemical Abstracts: | 2023:172551 |
| PMID (PubMed): | 36676428 |
| OpenAlex: | W4315647981 |