Conductive Silver Films with Tunable Surface Properties: Thickness, Roughness and Porosity Научная публикация

Журнал Applied Surface Science
ISSN: 0169-4332
Вых. Данные Год: 2023, Том: 629, Номер статьи : 157392, Страниц : 10 DOI: 10.1016/j.apsusc.2023.157392
Ключевые слова Janus membrane; Organosol; Porosity; Roughness; Silver film; Surface resistivity
Авторы Kolodin A.N. 1 , Bulavchenko O.A. 2 , Syrokvashin M.M. 1 , Maksimovskiy E.A. 1 , Bulavchenko A.I. 1
Организации
1 Nikolaev Institute of Inorganic Chemistry, Siberian Branch of the Russian Academy of Sciences, 3, Acad. Lavrentiev Avenue, Novosibirsk 630090, Russia
2 Boreskov Institute of Catalysis, Siberian Branch of the Russian Academy of Sciences, 5, Acad. Lavrentiev Avenue, Novosibirsk 630090, Russia

Информация о финансировании (2)

1 Российский фонд фундаментальных исследований 20-03-00017
2 Министерство образования и науки Российской Федерации FWUZ-2021-0002 (121031700315-2)

Реферат: The organasol of nanoparticles (3 M, the particle size 6 ± 1 nm) was synthesized by the silver nitrate reduction with hydrazine in the reverse emulsions stabilized by the sodium bis(2-ethylhexyl)sulfosuccinate. The obtained silver nanoparticle emulsion was concentrated using electrophoretic concentration. The silver nanoparticle films with tunable thickness (from 3.9 ± 0.2 to 1.7 ± 0.2 µm), porosity (from 26 ± 10 to 46 ± 12%), density (from 5.7 ± 1.5 to 7.8 ± 3.0 g/cm3), roughness (from 4 ± 2 to 131 ± 19 nm) and surface electrical resistivity (from 0.03 ± 0.01 to 0.10 ± 0.01 Ohm/□) were obtained. The sintering process of the silver nanoparticle films was studied by in situ XRD experiment using synchrotron radiation. The separation procedure for the metallic films from the solid substrates was proposed. The separated sintered silver nanoparticle film was considered as a Janus membrane. The wetting asymmetry of the obtained Janus membrane was of 39°. The obtained films were considered as promising functional material with the bactericidal and the electrical conductive properties. The obtained Janus membrane could be placed on the flexible polymer substrates.
Библиографическая ссылка: Kolodin A.N. , Bulavchenko O.A. , Syrokvashin M.M. , Maksimovskiy E.A. , Bulavchenko A.I.
Conductive Silver Films with Tunable Surface Properties: Thickness, Roughness and Porosity
Applied Surface Science. 2023. V.629. 157392 :1-10. DOI: 10.1016/j.apsusc.2023.157392 WOS Scopus РИНЦ CAPlus OpenAlex
Даты:
Поступила в редакцию: 19 февр. 2023 г.
Принята к публикации: 26 апр. 2023 г.
Опубликована online: 3 мая 2023 г.
Опубликована в печати: 30 авг. 2023 г.
Идентификаторы БД:
Web of science: WOS:001001243700001
Scopus: 2-s2.0-85158034844
РИНЦ: 54387603
Chemical Abstracts: 2023:958204
OpenAlex: W4367673723
Цитирование в БД:
БД Цитирований
Scopus 5
Web of science 5
OpenAlex 6
РИНЦ 3
Альметрики: