In Situ Synchrotron XRD Study of the Pr–Ce–Ni–O System Научная публикация
| Журнал |
Journal of Surface Investigation: X-Ray, Synchrotron and Neutron Techniques
ISSN: 1027-4510 , E-ISSN: 1819-7094 |
||||
|---|---|---|---|---|---|
| Вых. Данные | Год: 2023, Том: 17, Номер: 6, Страницы: 1302-1312 Страниц : 11 DOI: 10.1134/s1027451023060137 | ||||
| Ключевые слова | Ce-doped Pr2NiO4; praseodymium nickelate; Pr-doped ceria; in situ XRD; synchrotron XRD; oxygen mobility; oxygen release; oxygen incorporation; IT-SOFC cathode; intermediate temperature solid oxide fuel cell; fluorite lattice parameter; Pr7O12 | ||||
| Авторы |
|
||||
| Организации |
|
Информация о финансировании (1)
| 1 | Министерство науки и высшего образования Российской Федерации (с 15 мая 2018) | ГЗ-2021-2023 |
Реферат:
Samples of the Pr–Ce–Ni–O system with Ce content relative to Pr: 5, 25, 50 mol % were synthesized by a modified Pechini method and studied using in situ synchrotron XRD in the temperature range of 30–700–30°C first in an inert gas flow then in a synthetic air flow. The formation of a first-order Ruddlesden–Popper phase, as well as two cubic fluorite-type phases, was observed for a 5 mol % Ce : Pr sample. A sample with 25 mol % Ce : Pr comprised two fluorite phases. During heating in an inert gas flow, reversible Pr7O12-type phase formation was observed from some part of the fluorite phases. A sample with 50 mol % Ce : Pr comprised a single fluorite phase that turned out to be inhomogeneous with some close cation content distribution, which could be seen in the oxygen incorporation region upon heating in a synthetic air flow after thermocycling in an inert gas flow. It is seen under these conditions since the fluorite lattice parameter is sensitive to oxygen release (a sharp increase in the lattice parameters) and oxygen incorporation (a sharp decrease in the lattice parameters).
Библиографическая ссылка:
Mishchenko D.D.
, Arapova M.V.
, Shmakov A.N.
In Situ Synchrotron XRD Study of the Pr–Ce–Ni–O System
Journal of Surface Investigation: X-Ray, Synchrotron and Neutron Techniques. 2023. V.17. N6. P.1302-1312. DOI: 10.1134/s1027451023060137 WOS Scopus РИНЦ CAPlus OpenAlex СКИФ ID
In Situ Synchrotron XRD Study of the Pr–Ce–Ni–O System
Journal of Surface Investigation: X-Ray, Synchrotron and Neutron Techniques. 2023. V.17. N6. P.1302-1312. DOI: 10.1134/s1027451023060137 WOS Scopus РИНЦ CAPlus OpenAlex СКИФ ID
Даты:
| Поступила в редакцию: | 14 февр. 2023 г. |
| Принята к публикации: | 24 апр. 2023 г. |
| Опубликована в печати: | 8 дек. 2023 г. |
| Опубликована online: | 8 дек. 2023 г. |
Идентификаторы БД:
| Web of science: | WOS:001142593700035 |
| Scopus: | 2-s2.0-85178927584 |
| РИНЦ: | 56103352 |
| Chemical Abstracts: | 2023:2574151 |
| OpenAlex: | W4389488871 |
| СКИФ ID: | 1845 |
Цитирование в БД:
Пока нет цитирований