Реферат: The conversion of syngas into higher alcohols was examined using bimetallic Rh-Co, Rh-Cu, and multimetallic RhCuPd catalysts, all of which were supported on ZrO2. This process was also studied using a MnOx-promoted Rh/SiO2 catalyst. These experiments were conducted within a temperature range of 225–300 °C, under a pressure of 30 bar, and with a H2/CO ratio of 2. The catalysts were characterized using a variety of physicochemical methods, including Transmission Electron Microscopy (TEM), X-ray Diffraction (XRD), X-ray Photoelectron Spectroscopy (XPS), and Carbon Monoxide Diffuse Reflectance Infrared Fourier Transform Spectroscopy (CO DRIFTS). The Rh particle sizes in the fresh catalysts were found to be less than 3 nm. The Rh-Co catalyst supported on ZrO2 exhibited the highest selectivity to ethanol, achieving 38 % at a CO conversion rate of 58 % at 275 °C. This catalyst also demonstrated a chain growth probability of 0.35 for alcohols. A slightly higher chain growth probability was observed with the Rh-MnOx/SiO2 catalyst, although this also resulted in the formation of substantial amounts of acetic acid. Interestingly, this acetic acid could be converted into ketones when RhMnOx was used in conjunction with Pd/ZrO2.

Библиографическая ссылка: Lind N. , Aho A. , Eränen K. , Virtanen P. , Simakova I. , Mäki-Arvela P. , Murzin D.Y.
Transformation of Syngas to Valuable Oxygenated Products over Rh-MnOx/SiO2, Rh-Co/ZrO2 and Rh-Cu/ZrO2 Catalysts
Applied Catalysis A: General. 2024. V.683. 119852 :1-19. DOI: 10.1016/j.apcata.2024.119852 WOS Scopus CAPlusCA OpenAlex

Даты:

Поступила в редакцию:	4 апр. 2024 г.
Принята к публикации:	18 июн. 2024 г.
Опубликована online:	29 июн. 2024 г.
Опубликована в печати:	5 авг. 2024 г.

Идентификаторы БД:

Web of science:	WOS:001266098100001
Scopus:	2-s2.0-85197414808
Chemical Abstracts:	2024:1494460
Chemical Abstracts (print):	188:126564
OpenAlex:	W4400156406

Цитирование в БД: Пока нет цитирований

Альметрики: