Temperature-Programmed C18O2 SSITKA for Powders of Fast Oxide-Ion Conductors: Estimation of Oxygen Self-Diffusion coefﬁcients | Sciact - CRIS-система Института катализа

Temperature-Programmed C18O2 SSITKA for Powders of Fast Oxide-Ion Conductors: Estimation of Oxygen Self-Diffusion coefﬁcients Научная публикация

Журнал

Solid State Ionics
ISSN: 0167-2738

Вых. Данные

Год: 2015, Том: 271, Страницы: 69-72 Страниц : 4 DOI: 10.1016/j.ssi.2014.11.004

Ключевые слова

C18O2SSITKA, Doped lanthanum silicates, Doped zirconia, Fast oxide-ion conductors, Oxygen diffusion coefficient

Авторы

Sadykov V. ^1,2 , Sadovskaya E. ^1,2 , Bobin A. ¹ , Kharlamova T. ³ , Uvarov N. ^2,4 , Ulikhin A. ⁴ , Argirusis Ch. ⁵ , Sourkouni G. ⁶ , Stathopoulos V. ⁷

Организации

1	Boreskov Institute of Catalysis, pr. Lavrentieva, 5, Novosibirsk 630090, Russia
2	Novosibirsk State University, Novosibirsk 630090, Russia
3	Tomsk State University, Tomsk 634050, Russia
4	Institute of Solid State Chemistry and Mechanochemistry, Novosibirsk, Russia
5	School of Chemical Engineering, National Technical University of Athens, Athens 15780, Greece
6	Energy Research Center Niedersachsen, Goslar 38640, Germany
7	School of Technological Applications, Technological Educational Institute of Sterea Ellada, Psahna, 34400 Chalkida, Greece

Информация о финансировании (2)

1	Министерство образования и науки Российской Федерации
2	Ministry of Education and Religious Affairs European Commission	Архимед III - Фаза II (APACELL)

For powders of oxide-ion conductors based on Al/Fe-doped lanthanum silicates as well as Sc+Ce-doped zirconia, the temperature–programmed exchange with C18O2 in the SSITKA mode was applied for estimation of the oxygen self-diffusion coefﬁcients Do. Comparison with results obtained for dense ceramics of these electrolytes using SIMS isotope proﬁling and conductivity measurements demonstrated a reasonable agreement for powders sintered at high temperatures, thus providing required veriﬁcation of C18O2 SSITKA approach. For powders calcined at moderate temperatures much lower values of D O were obtained thus suggesting a strong negative effect of inhomogeneity of dopants spatial distribution on the oxygen mobility.

Sadykov V. , Sadovskaya E. , Bobin A. , Kharlamova T. , Uvarov N. , Ulikhin A. , Argirusis C. , Sourkouni G. , Stathopoulos V.
Temperature-Programmed C18O2 SSITKA for Powders of Fast Oxide-Ion Conductors: Estimation of Oxygen Self-Diffusion coefﬁcients
Solid State Ionics. 2015. V.271. P.69-72. DOI: 10.1016/j.ssi.2014.11.004 WOS Scopus РИНЦ CAPlusCA OpenAlex

Поступила в редакцию:	14 июл. 2014 г.
Принята к публикации:	4 нояб. 2014 г.
Опубликована online:	25 нояб. 2014 г.
Опубликована в печати:	1 мар. 2015 г.

Web of science:	WOS:000351961400011
Scopus:	2-s2.0-84923233276
РИНЦ:	24009475
Chemical Abstracts:	2014:1944101
Chemical Abstracts (print):	163:499020
OpenAlex:	W2012275967

БД	Цитирований
Web of science	29
Scopus	33
РИНЦ	33
OpenAlex	47