Synthesis and Functionalization of Filamentous Carbon Material via Decomposition of 1,2-dichlorethane over Self-Organizing Ni-Mo Catalyst Conference attendances

Language Английский
Participant type Устный
Conference 7th International Conference on Material Science and Engineering Technology
20-22 Oct 2018 , Beijing
Authors Bauman Yury Ivanovich 1 , Kibis Lidiya Sergeevna 1,2 , Mishakov Ilya Vladimirovich 1,3 , Rudneva Yu. V. 4 , Stoyanovskii Vladimir Olegovich 1 , Vedyagin Aleksey Anatolʹevich 1,3
Affiliations
1 Boreskov Institute of Catalysis SB RAS
2 Novosibirsk National Research University
3 National Research Tomsk Polytechnic University
4 Nikolaev Institute of Inorganic Chemistry SB RAS

Abstract: The laser engineered net shaping (LENS) system was used for the laser based manufacturing of a test geometry used to assess the performance of additive manufacturing systems. This system was preferred over a selective laser melting (SLM) system due to certain inherent benefits that would promote the manufacture of the test geometry where the SLM system had failed due to part delamination. The test geometry was successfully manufactured on the LENS system and machined to produce test specimen for mechanical testing and microstructural evaluation. Investigations revealed that the α-β lamellar microstructure was formed via in situ martensitic decomposition of the α‟ structure. This resulted in promising yield and tensile strengths in excess of 900 MPa and high tensile elongation up to 13%.
Cite: Bauman Y.I. , Kibis L.S. , Mishakov I.V. , Rudneva Y.V. , Stoyanovskii V.O. , Vedyagin A.A.
Synthesis and Functionalization of Filamentous Carbon Material via Decomposition of 1,2-dichlorethane over Self-Organizing Ni-Mo Catalyst
7th International Conference on Material Science and Engineering Technology 20-22 Oct 2018