Реферат: The adsorption of N2, O2, and Ar vapors on a number of supermicroporous tin dioxide and zirconia xerogels at 77.4 K was studied. The micropore volumes calculated with the use of sorbate densities at the corresponding temperature were found to be in satisfactory agreement for all of the sorbates. At the same time, the volumes of larger pores measured using nitrogen were greater than the values found with other sorbates. The previously found behavior of oxygen and nitrogen molecules in the geometrically restricted space of supermicropores was substantiated. In particular, this behavior manifests itself in a change in the adsorption properties of a unit surface area of supermicropores as compared with the surface of mesopores. However, the effects of this kind were not found for the argon–nitrogen sorbate pair.

Библиографическая ссылка: Gavrilov V.Y.
Adsorption of Nitrogen, Oxygen, and Argon Vapors on Supermicroporous Oxides
Kinetics and Catalysis. 2002. V.43. N4. P.580-584. DOI: 10.1023/A:1019847606640 WOS Scopus РИНЦ CAPlusCA OpenAlex

Оригинальная: Гаврилов В.Ю.
Адсорбция паров азота, кислорода и аргона на супермикропористых оксидах
Кинетика и катализ. 2002. Т.43. №4. С.628-633. РИНЦ

Даты:

Поступила в редакцию:	6 авг. 2001 г.
Опубликована в печати:	1 июл. 2002 г.

Идентификаторы БД:

Web of science:	WOS:000177849400020
Scopus:	2-s2.0-0038237947
РИНЦ:	13394635
Chemical Abstracts:	2002:627517
Chemical Abstracts (print):	137:284750
OpenAlex:	W88915545

Цитирование в БД:

БД	Цитирований
Scopus	1
OpenAlex	2

Альметрики: