Synthesis of Highly Dispersed Vanadium Diboride with the Use of Nanofibrous Carbon Научная публикация

Журнал Russian Journal of Applied Chemistry
ISSN: 1070-4272 , E-ISSN: 1608-3296
Вых. Данные Год: 2017, Том: 90, Номер: 9, Страницы: 1379-1385 Страниц : 7 DOI: 10.1134/S1070427217090014
Ключевые слова IRON BORIDE BATTERY; MOLECULAR-OXYGEN; METAL BORIDES; HIGH-CAPACITY; OXIDATION
Авторы Krutskii Yu.L. 1 , Maksimovskii E.A. 1,2 , Krutskaya T.M. 4 , Popov M.V. 1 , Netskina O.V. 3,5 , Nikulina A.A. 1 , Cherkasova N.Yu. 1 , Kvashina T.S. 1
Организации
1 Novosibirsk State Technical University, ul. Karla Marksa 20, Novosibirsk, 630073 Russia
2 Institute of Inorganic Chemistry, Siberian Branch, Russian Academy of Sciences, pr. Akademika Lavrent’eva 3, Novosibirsk, 630090 Russia
3 Novosibirsk State University, Novosibirsk, 630090 Russia
4 Novosibirsk State Architectural-Constructional University, ul. Turgeneva 198, Novosibirsk, 630008 Russia
5 Boreskov Institute of Catalysis, Siberian Branch, Russian Academy of Sciences, pr. Akademika Lavrent’eva 5, Novosibirsk, 630090 Russia

Информация о финансировании (1)

1 Министерство образования и науки Российской Федерации 02.G25.31.0144 от 01.12.2015

Реферат: Reduction of vanadium(III) oxide with boron carbide and nanofi brous carbon in an induction furnace in argon was used to obtain a highly dispersed vanadium diboride powder. The characteristics of vanadium diboride powders were studied by various analytical methods. It was found that the material obtained contains only a single phase, vanadium diboride, with powder particles mostly aggregated, the average size of particles and aggregates being 9.8 μm at a wide particle size distribution. The optimal synthesis parameters were determined: V2O3 : B4C : C ratio corresponding to the stoichiometry, temperature 1700°C, and keeping time 20 min.
Библиографическая ссылка: Krutskii Y.L. , Maksimovskii E.A. , Krutskaya T.M. , Popov M.V. , Netskina O.V. , Nikulina A.A. , Cherkasova N.Y. , Kvashina T.S.
Synthesis of Highly Dispersed Vanadium Diboride with the Use of Nanofibrous Carbon
Russian Journal of Applied Chemistry. 2017. V.90. N9. P.1379-1385. DOI: 10.1134/S1070427217090014 WOS Scopus РИНЦ CAPlusCA OpenAlex
Оригинальная: Крутский Ю.Л. , Максимовский Е.А. , Крутская Т.М. , Попов М.В. , Нецкина О.В. , Никулина А.А. , Черкасова Н.Ю. , Квашина Т.С.
Синтез высокодисперсного диборида ванадия с использованием нановолокнистого углерода
Журнал прикладной химии. 2017. Т.90. №9. С.1121-1127. РИНЦ
Даты:
Опубликована в печати: 1 сент. 2017 г.
Поступила в редакцию: 18 окт. 2017 г.
Опубликована online: 4 янв. 2018 г.
Идентификаторы БД:
Web of science: WOS:000419257800001
Scopus: 2-s2.0-85040126140
РИНЦ: 35494022
Chemical Abstracts: 2018:36456
Chemical Abstracts (print): 168:161946
OpenAlex: W2782314000
Цитирование в БД:
БД Цитирований
Web of science 4
Scopus 4
РИНЦ 5
OpenAlex 5
Альметрики: