Effect of Carbon Coating on Spontaneous C12A7 Whisker Formation Full article

Journal Applied Surface Science
ISSN: 0169-4332
Output data Year: 2018, Volume: 444, Pages: 336-338 Pages count : 3 DOI: 10.1016/j.apsusc.2018.03.056
Tags Calcium aluminate, Carbon nanoreactor, HRTEM, Structured carbon layers, Whiskers
Authors Zaikovskii Vladimir I. 1,2 , Volodin Alexander M. 1 , Stoyanovskii Vladimir O. 1 , Cherepanova Svetlana V. 1,2 , Vedyagin Aleksey A. 1,3
Affiliations
1 Boreskov Institute of Catalysis SB RAS, Novosibirsk 630090, Russia
2 Novosibirsk State University, Novosibirsk 630090, Russia
3 National Research Tomsk Polytechnic University, Tomsk 634050, Russia

Funding (1)

1 Russian Science Foundation 16-13-10168

Abstract: A carbon nanoreactor concept was applied to study the stabilization effect of carbon shell on phase composition and morphology of dodecacalcium hepta-aluminate Ca12Al14O33. The starting C12A7 powder was obtained using aluminum and calcium hydroxides as precursors. Carbon shell was formed by a chemical vapor deposition of divinyl at 550°C. After the calcination at 1400 °C, the product was characterized by X-ray diffraction analysis (XRD) and high resolution transmission electron microscopy (HRTEM). It was observed for a first time that spontaneous formation of calcium aluminate whiskers take place under the conditions described. Each whisker consists of a ‘head’ (globular particle of 0.5 microns in diameter) and a ‘tail’ (prolonged whisker of few microns in length and 0.1–0.2 microns in diameter). According to HRTEM, the ‘head’ is characterized with microcrystal lattice of Ca12Al14O33 compound. XRD data show the presence of CaAl2O4 phase traces. The ‘head’ and ‘tail’ of the whisker are covered with structured graphene layers of 10nm and 3nm, correspondingly.
Cite: Zaikovskii V.I. , Volodin A.M. , Stoyanovskii V.O. , Cherepanova S.V. , Vedyagin A.A.
Effect of Carbon Coating on Spontaneous C12A7 Whisker Formation
Applied Surface Science. 2018. V.444. P.336-338. DOI: 10.1016/j.apsusc.2018.03.056 WOS Scopus РИНЦ ANCAN OpenAlex
Dates:
Submitted: Oct 18, 2017
Accepted: Mar 8, 2018
Published online: Mar 9, 2018
Published print: Jun 1, 2018
Identifiers:
Web of science: WOS:000429343200040
Scopus: 2-s2.0-85043595331
Elibrary: 35544752
Chemical Abstracts: 2018:475095
Chemical Abstracts (print): 168:379816
OpenAlex: W2789826034
Citing:
DB Citing
Web of science 9
Scopus 9
Elibrary 9
OpenAlex 9
Altmetrics: