Реферат: A preparation procedure was developed, and samples of nanodisperse Fe3+ hydroxide with a narrow particle-size distribution (2.5–3.5 nm) were synthesized. The occurrence of a substructure in the bulk of Fe3+ hydroxide nanoparticles was detected for the first time using light-field and dark-field transmission electron microscopy. It was found that structurally ordered regions with sizes of ∼1.0 nm, which were disoriented with respect to each other at angles of a few degrees, occurred in the bulk of the nanoparticles. The empirical formula of nanodisperse iron hydroxide was ∼Fe2O3 · 1.8H2O; the structure of this hydroxide contained crystal water, OH−, and O2−. The coordination number of Fe3+ cations with respect to oxygen was 6. It was found that both structural and nonstructural water can be removed almost completely from the bulk of nanoparticles in the course of sample heating to 150–250°C in a vacuum with the retention of their amorphous character and observed sizes. In the course of dehydration, the mutual mobility of nanoparticles within aggregates was retained in Fe3+ xerogels; this resulted in a decrease in the total pore volume, whereas the volume of mesopores with diameters of 3.4–3.5 nm progressively increased. The micropore structure of the samples of nanodisperse iron hydroxides was studied by the molecular probe method using the low-temperature (77 K) sorption of nitrogen and molecular hydrogen. It was found that, along with micropores of volume ∼0.02 cm3/g, which are accessible to both of the sorbates, the sorption of H2 exhibited an additional specific absorption of 1.0–1.7 cm3(STP)/g, which can be interpreted as an additional ultramicropore volume accessible to only hydrogen molecules.

Библиографическая ссылка: Gavrilov V.Y. , Krivoruchko O.P.
Synthesis and Mesopore–Micropore Structure Characterization of Nanodisperse Fe3+ Hydrogels (Xerogels)
Kinetics and Catalysis. 2009. V.50. N1. P.122-130. DOI: 10.1134/S0023158409010169 WOS Scopus РИНЦ CAPlusCA OpenAlex

Оригинальная: Гаврилов В.Ю. , Криворучко О.П.
Синтез нанодисперсных гидро(ксеро) гелей Fe3+ и изучение их мезо- и микропористой структуры
Кинетика и катализ. 2009. Т.50. №1. С.132-140. РИНЦ

Даты:

Поступила в редакцию:	16 июл. 2007 г.
Опубликована в печати:	1 янв. 2009 г.
Опубликована online:	18 апр. 2009 г.

Идентификаторы БД:

Web of science:	WOS:000265298500016
Scopus:	2-s2.0-65249165369
РИНЦ:	13610112
Chemical Abstracts:	2009:328912
Chemical Abstracts (print):	150:481731
OpenAlex:	W2025177331

Цитирование в БД:

БД	Цитирований
Scopus	1
РИНЦ	1
OpenAlex	1

Альметрики: