Growth of Carbon Nanotubes from Butadiene on a Fe–Mo–Al2O3 Catalyst Научная публикация
| Журнал |
Kinetics and Catalysis
ISSN: 0023-1584 , E-ISSN: 1608-3210 |
||
|---|---|---|---|
| Вых. Данные | Год: 2010, Том: 51, Номер: 2, Страницы: 293-298 Страниц : 6 DOI: 10.1134/S0023158410020199 | ||
| Ключевые слова | DECOMPOSITION; FILAMENTS; MECHANISM; METHANE; IRON; CO | ||
| Авторы |
|
||
| Организации |
|
Информация о финансировании (2)
| 1 | Российский фонд фундаментальных исследований | 07-08-00339 |
| 2 | Президиум РАН | 139-522 |
Реферат:
The MoO3-Fe2O3-Al2O3 catalysts were prepared from metal nitrates using a coprecipitation method. It was found that the modification of an alumina-iron catalyst with molybdenum oxide resulted in the formation of a solid solution based on hematite, in which a portion of iron ions was replaced by aluminum and molybdenum ions. The MoO3-Fe2O3-Al2O3 catalyst was reduced with a reaction mixture at 700°C. Under the action of 1,3-butadiene diluted with hydrogen, the solid solution based on hematite was initially converted into magnetite and then into an Fe-Mo alloy. The modification of an alumina-iron catalyst with molybdenum oxide considerably changed its properties in the course of carbon nanotube formation. As the Mo content was increased, the yield of carbon nanotubes passed through a maximum. The optimum catalyst was 6.5% MoO3–55% Fe2O3-Al2O3. The addition of small amounts of MoO3 (to 6.5 wt %) to the aluminairon catalyst increased the dispersity and modified the properties of active metal particles: because of the formation of an Fe-Mo alloy, the rate of growth decreased but the stability of carbon nanotube growth and the yield of the nanotubes increased. A further increase in the molybdenum content decreased the yield because molybdenum is inactive in the test process.
Библиографическая ссылка:
Chesnokov V.V.
, Zaikovskii V.I.
, Chichkanʹ A.S.
, Buyanov R.A.
Growth of Carbon Nanotubes from Butadiene on a Fe–Mo–Al2O3 Catalyst
Kinetics and Catalysis. 2010. V.51. N2. P.293-298. DOI: 10.1134/S0023158410020199 WOS Scopus РИНЦ CAPlusCA OpenAlex
Growth of Carbon Nanotubes from Butadiene on a Fe–Mo–Al2O3 Catalyst
Kinetics and Catalysis. 2010. V.51. N2. P.293-298. DOI: 10.1134/S0023158410020199 WOS Scopus РИНЦ CAPlusCA OpenAlex
Оригинальная:
Чесноков В.В.
, Зайковский В.И.
, Чичкань А.С.
, Буянов Р.А.
Закономерности роста углеродных нанотрубок из бутадиена на катализаторе Fe–Mo–Al2O3
Кинетика и катализ. 2010. Т.51. №2. С.310-316. РИНЦ
Закономерности роста углеродных нанотрубок из бутадиена на катализаторе Fe–Mo–Al2O3
Кинетика и катализ. 2010. Т.51. №2. С.310-316. РИНЦ
Даты:
| Поступила в редакцию: | 23 дек. 2008 г. |
| Опубликована в печати: | 1 мар. 2010 г. |
| Опубликована online: | 24 апр. 2010 г. |
Идентификаторы БД:
| Web of science: | WOS:000277012300019 |
| Scopus: | 2-s2.0-77952088655 |
| РИНЦ: | 15330304 |
| Chemical Abstracts: | 2010:517663 |
| Chemical Abstracts (print): | 152:574471 |
| OpenAlex: | W1972234044 |