Experimental Redetermination of the Cu–Pd Phase Diagram | Sciact - CRIS-система Института катализа

Experimental Redetermination of the Cu–Pd Phase Diagram Научная публикация

Журнал

Journal of Alloys and Compounds
ISSN: 0925-8388 , E-ISSN: 1873-4669

Вых. Данные

Год: 2018, Том: 777, Страницы: 204-212 Страниц : 9 DOI: 10.1016/j.jallcom.2018.10.332

Ключевые слова

Copper; Experimental X–ray study; Nanoalloys; Palladium; Phase diagram

Авторы

Popov A.A. ¹ , Shubin Yu.V. ^1,2 , Plyusnin P.E. ^1,2 , Sharafutdinov M.R. ³ , Korenev S.V. ^1,2

Организации

1	Nikolaev Institute of Inorganic Chemistry SB RAS, Novosibirsk, Russia
2	Novosibirsk State University, Novosibirsk, Russia
3	Institute of Solid State Chemistry and Mechanochemistry SB RAS, Russia

The equilibrium Cu–Pd phase diagram has been experimentally reinvestigated in the 300–680 °C temperature region by powder XRD involving a high-temperature technique. To reduce the annealing time needed for the system to attain the equilibrium state, nanosized specimens with a characteristic crystallite size of 5–15 nm were used initially. All previously reported phases, i.e., a disordered face-centered cubic solid solution Cu1-xPdx (A1), a one-dimensional long-period superlattice structure Cu21Pd7 (1D–LPS), intermetallic compounds Cu3Pd (L12) and CuPd (B2), except a two-dimensional long-period superlattice structure (2D–LPS), could be confirmed. Homogeneity ranges of all solid phases existing in the Cu–Pd system were determined at distinct temperatures. The largest deviation of the solubility limits was observed for the Pd-rich boundary of the Cu3Pd region (25–30 at.% Pd) and the Cu-rich boundary of the Cu1-xPdx region in the compositional range >55 at.% Pd. Based on the present experimental results, the constitutional Cu–Pd diagram was modified.

Popov A.A. , Shubin Y.V. , Plyusnin P.E. , Sharafutdinov M.R. , Korenev S.V.
Experimental Redetermination of the Cu–Pd Phase Diagram
Journal of Alloys and Compounds. 2018. V.777. P.204-212. DOI: 10.1016/j.jallcom.2018.10.332 WOS Scopus OpenAlex CAPlusCA

Поступила в редакцию:	19 авг. 2018 г.
Принята к публикации:	25 окт. 2018 г.
Опубликована online:	27 окт. 2018 г.
Опубликована в печати:	10 мар. 2019 г.

≡ Web of science:	WOS:000454856800026
≡ Scopus:	2-s2.0-85056182118
≡ OpenAlex:	W2898176087
≡ Chemical Abstracts:	2018:2116453
≡ Chemical Abstracts (print):	170:20900

≡ Scopus	31	Сбор данных от 15.02.2026
≡ OpenAlex	30	Сбор данных от 15.02.2026
≡ Web of science	30	Сбор данных от 13.02.2026