Boron Carbonitride Films with Tunable Composition: LPCVD and PECVD Synthesis Using Trimethylamine Borane and Nitrogen Mixture and Characterization Научная публикация

Журнал Applied Sciences (Switzerland)
ISSN: 2076-3417
Вых. Данные Год: 2023, Том: 13, Номер: 8, Номер статьи : 4959, Страниц : 27 DOI: 10.3390/app13084959
Ключевые слова boron carbonitride films; boron carbide films; trimethylamine borane; mechanical properties; optical properties; wettability
Авторы Belaya Svetlana V. 1 , Maksimovsky Eugene A. 1 , Shayapov Vladimir R. 1 , Shapovalova Aleksandra A. 1 , Kolodin Alexey N. 1 , Saraev Andrey A. 2 , Asanov Igor P. 1 , Khomyakov Maxim N. 3 , Yushina Irina V. 1 , Plekhanov Aleksandr G. 1 , Sulyaeva Veronica S. 1 , Kosinova Marina L. 1
Организации
1 Nikolaev Institute of Inorganic Chemistry SB RAS, 3, Acad. Lavrentiev Ave., Novosibirsk 630090, Russia
2 Boreskov Institute of Catalysis SB RAS, 5, Acad. Lavrentiev Ave., Novosibirsk 630090, Russia
3 Institute of Laser Physics SB RAS, 15B, Acad. Lavrentiev Ave., Novosibirsk 630090, Russia

Информация о финансировании (1)

1 Министерство науки и высшего образования Российской Федерации (с 15 мая 2018) FWUZ-2021-0006 (121031700314-5)

Реферат: This study reports the chemical vapor deposition of amorphous boron carbonitride films on Si(100) and SiO2 substrates using a trimethylamine borane and nitrogen mixture. BCxNy films with different compositions were produced via variations in substrate temperature and type of gas-phase activation. The low-pressure chemical vapor deposition (LPCVD) and plasma-enhanced chemical vapor deposition (PECVD) methods were used. The “elemental composition—chemical bonding state—properties” relationship of synthesized BCxNy was systematically studied. The hydrophilicity, mechanical, and optical properties of the films are discussed in detail. The composition of films deposited by the LPCVD method at temperatures ranging from 673 to 973 K was close to that of boron carbide with a low nitrogen content (BCxNy). The refractive index of these films changed in the range from 2.43 to 2.56 and increased with temperature. The transparency of these films achieved 85%. LPCVD films were hydrophilic and the water contact angles varied between 53 and 63°; the surface free energy was 42–48 mN/m. The microhardness, Young’s modulus and elastic recovery of LPCVD films ranged within 24–28 GPa, 220–247 GPa, and 70–74%, respectively. The structure of the PECVD films was close to that of hexagonal boron nitride, and their composition can be described by the BCxNyOz:H formula. In case of the PECVD process, the smooth films were only produced at low deposition temperatures (373–523 K). The refractive index of these films ranged from 1.51 to 1.67. The transparency of these films achieved 95%; the optical band gap was evaluated as 4.92–5.28 eV. Unlike LPCVD films, they were very soft, and their microhardness, Young’s modulus and elastic recovery were 0.8–1.4 GPa, 25–26 GPa, and 19–28%, respectively. A set of optimized process parameters to fabricate LPCVD BCxNy films with improved mechanical and PECVD films with high transparency is suggested.
Библиографическая ссылка: Belaya S.V. , Maksimovsky E.A. , Shayapov V.R. , Shapovalova A.A. , Kolodin A.N. , Saraev A.A. , Asanov I.P. , Khomyakov M.N. , Yushina I.V. , Plekhanov A.G. , Sulyaeva V.S. , Kosinova M.L.
Boron Carbonitride Films with Tunable Composition: LPCVD and PECVD Synthesis Using Trimethylamine Borane and Nitrogen Mixture and Characterization
Applied Sciences (Switzerland). 2023. V.13. N8. 4959 :1-27. DOI: 10.3390/app13084959 WOS Scopus РИНЦ CAPlusCA OpenAlex
Даты:
Поступила в редакцию: 10 мар. 2023 г.
Принята к публикации: 11 апр. 2023 г.
Опубликована в печати: 14 апр. 2023 г.
Опубликована online: 14 апр. 2023 г.
Идентификаторы БД:
Web of science: WOS:000977755200001
Scopus: 2-s2.0-85156172523
РИНЦ: 54387378
Chemical Abstracts: 2023:879388
Chemical Abstracts (print): 2023:879388
OpenAlex: W4365509100
Цитирование в БД:
БД Цитирований
Scopus 4
Web of science 4
OpenAlex 3
РИНЦ 4
Альметрики: