Oxygen Dissolution in Polycrystalline Palladium at O2 Pressures of 0.1 to 100 Pa Научная публикация
| Журнал |
Kinetics and Catalysis
ISSN: 0023-1584 , E-ISSN: 1608-3210 |
||
|---|---|---|---|
| Вых. Данные | Год: 2013, Том: 54, Номер: 1, Страницы: 106-118 Страниц : 13 DOI: 10.1134/S0023158413010114 | ||
| Ключевые слова | Palladium; Oxide Film; Subsurface Layer; Oxide Film Surface; Palladium Oxide | ||
| Авторы |
|
||
| Организации |
|
Реферат:
Oxygen dissolution in polycrystalline palladium Pd(poly) at O2 pressures ( PO2) of 0.1 to 100 Pa and a temperature of 600 K has been investigated by temperature-programmed desorption. The dissolution process under these conditions includes O2 chemisorption on the oxide film surface, the insertion of Oads atoms under the oxide layer, and their diffusion into the subsurface layers of palladium. During chemisorption, a structure ensuring that the Oads coverage of the surface increases with increasing PO2 forms on the surface of the oxide film. This is favorable for Oads penetration through the oxide film and increases the amount of absorbed oxygen. The Oads coverage of the surface calculated via the Langmuir equation at an O2 desorption activation energy of E des = 125 kJ/mol correlates with the number of absorbed oxygen monolayers (n). At n ≥ 1, oxygen absorption by Pd(poly) is due to the diffusion of O atoms in the palladium lattice. After the accumulation of 14–18 oxygen monolayers in the subsurface layers of palladium, oxygen absorption practically stops depending on PO2. Thus, the acceleration of oxygen dissolution in palladium is due to the formation of the surface oxide film and the increase in the Oads coverage of this film, which facilitates the insertion of Oads atoms into the subsurface layers of palladium.
Библиографическая ссылка:
Salanov A.N.
, Suprun E.A.
Oxygen Dissolution in Polycrystalline Palladium at O2 Pressures of 0.1 to 100 Pa
Kinetics and Catalysis. 2013. V.54. N1. P.106-118. DOI: 10.1134/S0023158413010114 WOS Scopus РИНЦ CAPlusCA OpenAlex
Oxygen Dissolution in Polycrystalline Palladium at O2 Pressures of 0.1 to 100 Pa
Kinetics and Catalysis. 2013. V.54. N1. P.106-118. DOI: 10.1134/S0023158413010114 WOS Scopus РИНЦ CAPlusCA OpenAlex
Оригинальная:
Саланов А.Н.
, Супрун Е.А.
Растворение кислорода в поликристаллическом палладии при давлениях О2 от 0.1 до 100 Па
Кинетика и катализ. 2013. Т.54. №1. С.111-125. DOI: 10.7868/S0453881113010115 РИНЦ OpenAlex
Растворение кислорода в поликристаллическом палладии при давлениях О2 от 0.1 до 100 Па
Кинетика и катализ. 2013. Т.54. №1. С.111-125. DOI: 10.7868/S0453881113010115 РИНЦ OpenAlex
Даты:
| Поступила в редакцию: | 26 мар. 2012 г. |
| Опубликована в печати: | 1 янв. 2013 г. |
| Опубликована online: | 5 февр. 2013 г. |
Идентификаторы БД:
| Web of science: | WOS:000314534800013 |
| Scopus: | 2-s2.0-84873361108 |
| РИНЦ: | 20427192 |
| Chemical Abstracts: | 2013:197850 |
| Chemical Abstracts (print): | 158:516052 |
| OpenAlex: | W2032912741 |