Mechanisms of Pd(1 1 0) Surface Reconstruction and Oxidation: XPS, LEED and TDS Study Научная публикация
| Конференция |
23rd European Conference on Surface Science 04-09 сент. 2005 , Berlin |
||
|---|---|---|---|
| Журнал |
Surface Science
ISSN: 0039-6028 |
||
| Вых. Данные | Год: 2006, Том: 600, Номер: 18, Страницы: 4119-4125 Страниц : 7 DOI: 10.1016/j.susc.2006.01.131 | ||
| Ключевые слова | Catalysis, Chemisorption, Oxidation, Palladium, Single crystal surfaces, Thermal desorption spectroscopy, X-ray photoelectron spectroscopy | ||
| Авторы |
|
||
| Организации |
|
Информация о финансировании (1)
| 1 | Российский фонд фундаментальных исследований | 03-03-33177 |
Реферат:
Oxygen interaction with Pd(1 1 0) has been studied in a wide range of pressures (Po2 = 10−6–100 Pa) and temperatures (T = 400–600 K) by X-ray photoelectron spectroscopy (XPS), low energy electron diffraction (LEED) and thermal desorption spectroscopy (TDS). The amount of oxygen absorbed by Pd(1 1 0) single crystal grows to more than 100 ML when the reaction temperature and the O2 exposure are increased. Several reconstructed and oxide structures are sequentially formed on Pd(1 1 0) as the amount of adsorbed and absorbed oxygen increases. During oxygen adsorption (1 × 2) reconstruction occurs and a c(2 × 4) structure is formed on Pd(1 1 0) at θ = 0.5 ML. When the amount of absorbed oxygen increases from 0.5 to 2.0 ML, oxygen penetrates into subsurface Pd layers to the depth exceeding 15–20 Å while retaining the c(2 × 4) structure. When the amount of absorbed oxygen is between 2 and 5 ML, the surface is subjected to reconstruction with the formation of a surface oxide with θ ∼ 0.8 that has a complex LEED diffraction pattern. Further increase of the amount of absorbed oxygen beyond 5 ML leads to oxygen location in the subsurface region forming PdO clusters. They gradually grow to form an almost continuous layer composed of PdO clusters.
Библиографическая ссылка:
Titkov A.I.
, Salanov A.N.
, Koshcheev S.V.
, Boronin A.I.
Mechanisms of Pd(1 1 0) Surface Reconstruction and Oxidation: XPS, LEED and TDS Study
Surface Science. 2006. V.600. N18. P.4119-4125. DOI: 10.1016/j.susc.2006.01.131 WOS Scopus РИНЦ CAPlusCA OpenAlex
Mechanisms of Pd(1 1 0) Surface Reconstruction and Oxidation: XPS, LEED and TDS Study
Surface Science. 2006. V.600. N18. P.4119-4125. DOI: 10.1016/j.susc.2006.01.131 WOS Scopus РИНЦ CAPlusCA OpenAlex
Даты:
| Опубликована online: | 8 мая 2006 г. |
| Опубликована в печати: | 15 сент. 2006 г. |
Идентификаторы БД:
| Web of science: | WOS:000241450600122 |
| Scopus: | 2-s2.0-33748932691 |
| РИНЦ: | 13532557 |
| Chemical Abstracts: | 2006:1023224 |
| Chemical Abstracts (print): | 146:13907 |
| OpenAlex: | W2000655002 |