Structure Modification of Different Graphite and Glassy Carbon Surfaces Under High Power Action by Hydrogen Plasma | Sciact - CRIS-система Института катализа

Structure Modification of Different Graphite and Glassy Carbon Surfaces Under High Power Action by Hydrogen Plasma Научная публикация

Конференция

8th International Conference on Open Magnetic Systems for Plasma Confinement
05-09 июл. 2010 , Новосибирск

Журнал

Fusion Science and Technology
ISSN: 1536-1055

Вых. Данные

Год: 2011, Том: 59, Номер: 1T, Страницы: 268-270 Страниц : 3

Ключевые слова

Crystallite size; Glass; Graphite; Surface treatment

Авторы

Shoshin A.A. ^1,2 , Arzhannikov A.V. ^1,2 , Burdakov A.V. ¹ , Kuklin K.N. ¹ , Ivanov I.A. ^1,2 , Mekler K.I. ¹ , Polosatkin S.V. ^1,2 , Postupaev V.V. ^1,2 , Raspopin K.S. ³ , Rovenskikh A.F. ¹ , Simonov P.A. ³ , Sinitsky S.L. ^1,2 , Snytnikov V.N. ³

Организации

1	Budker Institute of Nuclear Physics, 11 Lavrentjev Avenue, Novosibirsk, 630090, Russia
2	Novosibirsk State University, 2 Pirogova Street, Novosibirsk, 630090, Russia
3	Boreskov Institute of Catalysis, 5 Lavrentjev Avenue, Novosibirsk, 630090, Russia

Информация о финансировании (8)

1	Министерство образования и науки Российской Федерации	2.1.1/3983
2	Министерство образования и науки Российской Федерации	2.1.1./3465
3	Министерство образования и науки Российской Федерации	P2309
4	Министерство образования и науки Российской Федерации	P276
5	Министерство образования и науки Российской Федерации	02.518.11.7113
6	Министерство образования и науки Российской Федерации	14.740.11.0053
7	Президиум РАН	30
8	Сибирское отделение Российской академии наук	33

The studies of exposing of targets by hot-electron plasma exhaust from the multi-mirror trap GOL-3 are carried out. The results of Raman and SEM studies of surface modification of carbon materials with different ordering range of sp2 fraction (different graphite and glassy carbon) exposed by pulsed hot hydrogen plasma with energy density up to 8 MJ/m2 are presented. It is shown that on the depth up to ~80 nm due to this exposing there are obtained two effects—micro structural destruction of the surface and extension of crystallite size of sp2 phase, i.e. ordering of nanostructure.

Shoshin A.A. , Arzhannikov A.V. , Burdakov A.V. , Kuklin K.N. , Ivanov I.A. , Mekler K.I. , Polosatkin S.V. , Postupaev V.V. , Raspopin K.S. , Rovenskikh A.F. , Simonov P.A. , Sinitsky S.L. , Snytnikov V.N.
Structure Modification of Different Graphite and Glassy Carbon Surfaces Under High Power Action by Hydrogen Plasma
Fusion Science and Technology. 2011. V.59. N1T. P.268-270. WOS Scopus РИНЦ OpenAlex CAPlusCA

Опубликована в печати:

1 янв. 2011 г.

≡ Web of science:	WOS:000288974200070
≡ Scopus:	2-s2.0-79952829239
≡ РИНЦ:	16839879
≡ OpenAlex:	W194565799
≡ Chemical Abstracts:	2011:272012
≡ Chemical Abstracts (print):	156:188623

≡ Web of science	10	Сбор данных от 13.02.2026
≡ Scopus	10	Сбор данных от 15.02.2026
≡ РИНЦ	9	Сбор данных от 15.02.2026
≡ OpenAlex	10	Сбор данных от 15.02.2026