IRS Study of Ethylene Polymerization Catalyst SiO2/Methylaluminoxane/Zirconocene Научная публикация
| Журнал |
Journal of Molecular Catalysis A: Chemical
ISSN: 1381-1169 |
||
|---|---|---|---|
| Вых. Данные | Год: 1999, Том: 142, Номер: 1, Страницы: 27-37 Страниц : 11 DOI: 10.1016/S1381-1169(98)00275-1 | ||
| Ключевые слова | Ethylene polymerization, IR spectroscopy, Lewis acidic sites, Methylaluminoxane, Silica supported catalyst, Supported metallocene catalysts, Trimethylaluminium | ||
| Авторы |
|
||
| Организации |
|
Информация о финансировании (1)
| 1 | Российский фонд фундаментальных исследований | 97-03-32546 |
Реферат:
IR spectroscopy has been used to study the interaction of silica with two methylaluminoxane (MAO) samples differed by trimethylaluminium (TMA) content and with TMA. MAO and TMA have been shown to react with silica in a different way. Whereas TMA interacts with terminal hydroxyl groups of silica via the protolysis reaction, MAO mainly adsorbs on the surface hydroxyl groups of silica without noticeable protolytical reaction with them. When silica is treated with commercial grade MAO with significant TMA content, the silica surface hydroxyl groups mainly interacts with TMA and MAO adsorbs on the surface of SiO2/TMA sample. Lewis acidic sites (LAS) of silica, modified with TMA and MAO samples differed by TMA content, have been investigated by IR spectroscopy (CO adsorption as probe molecule at 77 K). Two types of LAS were found on the surface of silica modified with MAO and TMA: LAS of moderate strength (νCO=2204–2212 cm−1) and weak LAS (νCO=2194 cm−1). The concentration of these acidic sites was estimated. By anchoring of Cp2ZrCl2 on silica, modified with TMA and MAO, the corresponding catalysts SiO2/TMA/Cp2ZrCl2 and SiO2/MAO/Cp2ZrCl2 were prepared and tested at ethylene polymerization. Some correlations between the amount and strength of surface LAS of supports, catalysts composition and their activity are discussed. It is proposed that the surface active species are formed at zirconocene interaction with the most strong LAS.
Библиографическая ссылка:
Panchenko V.N.
, Semikolenova N.V.
, Danilova I.G.
, Paukshtis E.A.
, Zakharov V.A.
IRS Study of Ethylene Polymerization Catalyst SiO2/Methylaluminoxane/Zirconocene
Journal of Molecular Catalysis A: Chemical. 1999. V.142. N1. P.27-37. DOI: 10.1016/S1381-1169(98)00275-1 WOS Scopus РИНЦ CAPlusCA OpenAlex
IRS Study of Ethylene Polymerization Catalyst SiO2/Methylaluminoxane/Zirconocene
Journal of Molecular Catalysis A: Chemical. 1999. V.142. N1. P.27-37. DOI: 10.1016/S1381-1169(98)00275-1 WOS Scopus РИНЦ CAPlusCA OpenAlex
Даты:
| Поступила в редакцию: | 19 дек. 1997 г. |
| Принята к публикации: | 4 авг. 1998 г. |
| Опубликована online: | 16 апр. 1999 г. |
| Опубликована в печати: | 20 мая 1999 г. |
Идентификаторы БД:
| Web of science: | WOS:000079772200004 |
| Scopus: | 2-s2.0-0033586960 |
| РИНЦ: | 13328255 |
| Chemical Abstracts: | 1999:220341 |
| Chemical Abstracts (print): | 131:45139 |
| OpenAlex: | W1982018586 |