Particle Size and Composition of Heat-Treated Aluminum-Iridium Catalysts Научная публикация
Журнал |
Kinetics and Catalysis
ISSN: 0023-1584 , E-ISSN: 1608-3210 |
||
---|---|---|---|
Вых. Данные | Год: 1979, Том: 20, Номер: 1, Страницы: 138-141 Страниц : 4 | ||
Авторы |
|
||
Организации |
|
Реферат:
The x-ray diffraction study of the changes of dispersion of Ir in Ir/Al2O3 catalyst, pretreated at 500-1100° in H or in oxidizing medium (Ar containing 0.003% O), revealed that the stability of dispersed compounds depends on the composition of gaseous phase and on reaction of the active component with the support (here reaction of H2IrCl6 with γ-, η, or δ- Al2O3). The polymorphic transition of alumina enhances reduction of the ionic part of Ir-support complex. A decomposition of this complex leads to the formation of very fine metal particles.
Библиографическая ссылка:
Moroz E.M.
, Bogdanov S.V.
, Ushakov V.A.
, Levitskii E.A.
Particle Size and Composition of Heat-Treated Aluminum-Iridium Catalysts
Kinetics and Catalysis. 1979. V.20. N1. P.138-141. WOS РИНЦ
Particle Size and Composition of Heat-Treated Aluminum-Iridium Catalysts
Kinetics and Catalysis. 1979. V.20. N1. P.138-141. WOS РИНЦ
Оригинальная:
Мороз Э.М.
, Богданов С.В.
, Ушаков В.А.
, Левицкий Э.А.
Дисперсность и состав термообработанных алюмоиридиевых катализаторов
Кинетика и катализ. 1979. Т.20. №1. С.173-176. РИНЦ
Дисперсность и состав термообработанных алюмоиридиевых катализаторов
Кинетика и катализ. 1979. Т.20. №1. С.173-176. РИНЦ