Dynamic Magnetization of ε-Fe2O3 in Pulse Field: Evidence of Ssurface Effect
Научная публикация
| Общая информация |
Язык:
Английский,
Жанр:
Статья (Full article),
Статус опубликования:
Опубликована,
Оригинальность:
Оригинальная
|
| Журнал |
Journal of Applied Physics
ISSN: 0021-8979
, E-ISSN: 1089-7550
|
| Вых. Данные |
Год: 2015,
Том: 117,
Страницы: 063908
Страниц
: 6
DOI:
10.1063/1.4907586
|
| Авторы |
Balaev D.A.
1,2
,
Poperechny I.S.
3,4
,
Krasikov A.A.
2
,
Shaikhutdinov K.A.
1
,
Dubrovskiy A.A.
1
,
Popkov S.I.
1
,
Balaev A.D.
1
,
Yakushkin S.S.
5
,
Bukhtiyarova G.A.
5
,
Martyanov O.N.
5
,
Raikher Yu.L.
3,6
|
| Организации |
| 1 |
Kirensky Institute of Physics, Russian Academy of Sciences, Siberian Branch, Krasnoyarsk 660036, Russia
|
| 2 |
Siberian Federal University, Krasnoyarsk 660041, Russia
|
| 3 |
Institute of Continuous Media Mechanics, Russian Academy of Sciences, Ural Branch, Perm 614013, Russia
|
| 4 |
Perm National Research Polytechnic University, Perm 614990, Russia
|
| 5 |
Boreskov Institute of Catalysis, Russian Academy of Sciences, Siberian Branch, Novosibirsk 630090, Russia
|
| 6 |
Уральский федеральный университет имени первого Президента России Б.Н. Ельцина
|
|
Информация о финансировании (3)
|
1
|
Российский фонд фундаментальных исследований
|
12-02-00897 (01201257702)
|
|
2
|
Российский фонд фундаментальных исследований
|
14-02-96002 (01201457919)
|
|
3
|
Пермский национальный исследовательский политехнический университет
|
MIG S26/617
|
The magnetization dynamics of ε-Fe2O3 nanoparticles with an average size of about 9 nm is investigated. From comparison of the hysteresis loops obtained in quasi-static conditions and under pulse fields with amplitudes up to 200 kOe and pulse lengths 8–32 ms, it follows that the effective coercivity increases considerably with the variation rate of the imposed magnetic field. A theoretical explanation of this behavior is proposed. The model takes into account the superparamagnetic effects as well as the fact that magnetic anisotropy of the nanoparticles, along with the bulk term, includes a surface contribution. The latter, being of minor importance for the observed magnetic behavior of 25–100 nm particles, becomes essential when the particle size is below 10 nm. From the experimental data, a reference value of the surface anisotropy of nanodisperse ε-Fe2O3 is established, and evidence is presented to the effect that below 300 K this contribution does not significantly depend on temperature.