Реферат: The radio frequency (RF) discharge in an oxygen atmosphere was used to produce metal oxide films. The high efficiency of the RF discharge technique for metal oxidation at room temperature was demonstrated for gold, silver and copper foils. Oxide films up to 10 nm in thickness were obtained. The produced oxide films were studied by X-ray photoelectron spectroscopy (XPS). The XPS data showed the formation of oxidised species: Cu2+, Ag1+ and Au3+. Analysis of the oxygen species was performed using O1s spectra. For copper and silver foils, the formation of additional oxygen species apart from oxygen in the structure of oxides was shown. The reaction probability toward oxidation of carbon monoxide (CO) was estimated for all oxidised layers. It was established that gold and silver oxide films interacted with CO at room temperature, while cupric oxide showed high activity at temperature >353 K.

Библиографическая ссылка: Stadnichenko A.I. , Kibis L.S. , Svintsitskiy D.A. , Koshcheev S.V. , Boronin A.I.
Application of RF Discharge in Oxygen to Create Highly Oxidized Metal Layers
Surface Engineering. 2018. V.34. N1. P.1-5. DOI: 10.1179/1743294415Y.0000000010 WOS Scopus РИНЦ CAPlusCA OpenAlex

Даты:

Поступила в редакцию:	13 авг. 2014 г.
Принята к публикации:	9 янв. 2015 г.
Опубликована online:	23 февр. 2016 г.
Опубликована в печати:	2 янв. 2018 г.

Идентификаторы БД:

Web of science:	WOS:000428130000001
Scopus:	2-s2.0-84978521866
РИНЦ:	31017244
Chemical Abstracts:	2015:144827
Chemical Abstracts (print):	167:559762
OpenAlex:	W2044977792

Цитирование в БД:

БД	Цитирований
Web of science	9
Scopus	8
РИНЦ	8
OpenAlex	7

Альметрики: