A Large Anisotropic Plasticity of L-Leucinium Hydrogen Maleate Preserved at Cryogenic Temperatures | Sciact - CRIS-система Института катализа

A Large Anisotropic Plasticity of L-Leucinium Hydrogen Maleate Preserved at Cryogenic Temperatures Научная публикация

Журнал

Acta Crystallographica Section B: Structural Science, Crystal Engineering and Materials
ISSN: 2052-5192 , E-ISSN: 2052-5206

Вых. Данные

Год: 2019, Том: 75 B, Номер: 2, Страницы: 143-151 Страниц : 9 DOI: 10.1107/s2052520619000441

Ключевые слова

plastic crystals; low temperature; hydrogen bonds; intermolecular interactions

Авторы

Arkhipov S.G. ^1,2,3 , Losev E.A. ^1,2,3 , Nguyen T.T. ¹ , Rychkov D.A. ^1,2 , Boldyreva E.V. ^1,3

Организации

1	Novosibirsk State University, Pirogova str. 2, Novosibirsk, 630090, Russian Federation
2	Institute of Solid State Chemistry and Mechanochemistry SB RAS, Novosibirsk, 630128, Russian Federation
3	Boreskov Institute of Catalysis SB RAS, Lavrentiev Ave. 5, Novosibirsk, 630090, Russian Federation

Информация о финансировании (4)

1	Российский фонд фундаментальных исследований	16-33-60089 (АААА-А16-116021550280-1)
2	Министерство науки и высшего образования Российской Федерации (с 15 мая 2018)	0239-2019-0003
3	Российский фонд фундаментальных исследований	18-43-543004 (АААА-А18-118061890006-6)
4	Министерство образования и науки Российской Федерации	Проект 5-100

L-Leucinium hydrogen maleate crystals are very plastic at ambient conditions. Here it is shown that this plasticity is preserved at least down to 77 K. The structural changes in the temperature range 293–100 K were followed in order to rationalize the large anisotropic plasticity in this compound. To the best of our knowledge, this is the first reported example of an organic compound remaining so plastic at cryogenic conditions.

Arkhipov S.G. , Losev E.A. , Nguyen T.T. , Rychkov D.A. , Boldyreva E.V.
A Large Anisotropic Plasticity of L-Leucinium Hydrogen Maleate Preserved at Cryogenic Temperatures
Acta Crystallographica Section B: Structural Science, Crystal Engineering and Materials. 2019. V.75 B. N2. P.143-151. DOI: 10.1107/s2052520619000441 WOS Scopus РИНЦ CAPlus OpenAlex

Поступила в редакцию:	6 дек. 2018 г.
Принята к публикации:	8 янв. 2019 г.
Опубликована online:	13 мар. 2019 г.
Опубликована в печати:	1 апр. 2019 г.

Web of science:	WOS:000463912400005
Scopus:	2-s2.0-85063033352
РИНЦ:	45554420
Chemical Abstracts:	2019:733580
OpenAlex:	W2921647223

БД	Цитирований
Scopus	16
Web of science	16
РИНЦ	17
OpenAlex	17