Study of the Chemical and Phase Transformations in the Mechanochemical Synthesis of the MgAl-Layered Double Hydroxide Научная публикация

Журнал Journal of Alloys and Compounds
ISSN: 0925-8388 , E-ISSN: 1873-4669
Вых. Данные Год: 2022, Том: 890, Номер статьи : 161902, Страниц : 12 DOI: 10.1016/j.jallcom.2021.161902
Ключевые слова Layered double hydroxides; Mechanochemical activation; Structural properties
Авторы Stepanova L.N. 1 , Kobzar E.O. 1 , Leont’eva N.N. 1 , Gulyaeva T.I. 1 , Vasilevich A.V. 1 , Babenko A.V. 1 , Serkova A.N. 2 , Salanov A.N. 2 , Belskaya O.B. 1
Организации
1 Center of New Chemical Technologies BIC, Boreskov Institute of Catalysis, Neftezavodskaya Str., 54, 644040 Omsk, Russia
2 Boreskov Institute of Catalysis, 5 Acad. Lavrentieva Ave., 630090 Novosibirsk, Russia

Информация о финансировании (1)

1 Министерство науки и высшего образования Российской Федерации (с 15 мая 2018) 0239-2021-0004

Реферат: Mechanochemical synthesis of MgAl-layered double hydroxides (MgAl-LDH) with molar ratio MgAl = 3 was performed. The effect of the acceleration of milling bodies (500 and 1000 m s-2), activation time (5–90 min), and water addition on the phase composition of obtained samples, their structural parameters, as well as on the process of formation of mixed oxides, prepared after LDH calcination was studied. The conditions for the preparation of single-phase LDH were established. It was shown the possibility of the textural properties regulation of mixed oxides by change of the mechanochemical synthesis parameters of corresponding layered double hydroxides.
Библиографическая ссылка: Stepanova L.N. , Kobzar E.O. , Leont’eva N.N. , Gulyaeva T.I. , Vasilevich A.V. , Babenko A.V. , Serkova A.N. , Salanov A.N. , Belskaya O.B.
Study of the Chemical and Phase Transformations in the Mechanochemical Synthesis of the MgAl-Layered Double Hydroxide
Journal of Alloys and Compounds. 2022. V.890. 161902 :1-12. DOI: 10.1016/j.jallcom.2021.161902 WOS Scopus РИНЦ CAPlus OpenAlex ЦНХТ ID
Даты:
Поступила в редакцию: 16 июн. 2021 г.
Принята к публикации: 5 сент. 2021 г.
Опубликована online: 8 сент. 2021 г.
Опубликована в печати: 15 янв. 2022 г.
Идентификаторы БД:
Web of science: WOS:000706854400003
Scopus: 2-s2.0-85114925794
РИНЦ: 47102763
Chemical Abstracts: 2021:2045531
OpenAlex: W3197845296
ЦНХТ ID: 3569
Цитирование в БД:
БД Цитирований
Scopus 17
РИНЦ 14
Web of science 16
OpenAlex 18
Альметрики: