Synthesis and Study of the Physicochemical Properties of the High-Temperature Supports MgO-Al2O3-SiO2 and MgO-Al2O3-ZrO2 Научная публикация
Журнал |
Kinetics and Catalysis
ISSN: 0023-1584 , E-ISSN: 1608-3210 |
||
---|---|---|---|
Вых. Данные | Год: 1989, Том: 30, Номер: 5, Страницы: 1016-1022 Страниц : 7 | ||
Авторы |
|
||
Организации |
|
Реферат:
The influence of the nature and initial ratio of components on phase composition, structure, and stability of high-temperature supports based on MgO-Al2O3-MO2 (M = Si,Zr) was studied at 1000-1550°. The Mg-Al-Si oxide samples contain more phases than do the Mg-Al-Zr oxide samples. The Mg-Al-Zr oxide supports prepared from hydrargillite exhibit higher thermal stability than the Mg-Al-Si oxide samples prepared at >1250° from melts derived from a mixture of SiO2 and MgSiO3. Mechanical stability decreases as sample overall pore volume increases.
Библиографическая ссылка:
Ivanova A.S.
, Dzisʹko V.A.
, Moroz E.M.
Synthesis and Study of the Physicochemical Properties of the High-Temperature Supports MgO-Al2O3-SiO2 and MgO-Al2O3-ZrO2
Kinetics and Catalysis. 1989. V.30. N5. P.1016-1022. WOS РИНЦ
Synthesis and Study of the Physicochemical Properties of the High-Temperature Supports MgO-Al2O3-SiO2 and MgO-Al2O3-ZrO2
Kinetics and Catalysis. 1989. V.30. N5. P.1016-1022. WOS РИНЦ
Оригинальная:
Иванова А.С.
, Дзисько В.А.
, Мороз Э.М.
Синтез и исследование физико-химических свойств высокотемпературных носителей MgO – Al2O3 – SiO2 и MgO – Al2O3 – ZrO2
Кинетика и катализ. 1989. Т.30. №5. С.1167-1173. РИНЦ
Синтез и исследование физико-химических свойств высокотемпературных носителей MgO – Al2O3 – SiO2 и MgO – Al2O3 – ZrO2
Кинетика и катализ. 1989. Т.30. №5. С.1167-1173. РИНЦ
Даты:
Поступила в редакцию: | 15 апр. 1988 г. |
Опубликована в печати: | 1 сент. 1989 г. |
Идентификаторы БД:
Web of science | WOS:A1989DH96500006 |
РИНЦ | 24497561 |
Цитирование в БД:
Пока нет цитирований