Nanocrystalline Ultra High Surface Area Magnesium Oxide as a Selective Base Catalyst Научная публикация
Журнал |
Scripta Materialia
ISSN: 1359-6462 |
||||
---|---|---|---|---|---|
Вых. Данные | Год: 2001, Том: 44, Номер: 8-9, Страницы: 1663-1666 Страниц : 4 DOI: 10.1016/S1359-6462(01)00877-6 | ||||
Ключевые слова | Aero-gel, Catalysis, Electron spin resonance, Nanocrystal, Surface, TEM | ||||
Авторы |
|
||||
Организации |
|
Реферат:
Nanocyrstals of MgO having 4 nm average crystallite sizes with 450–550 m2/g surface area were prepared by the Aero-gel preparation method (AP-MgO). Dehydrohalogenation of 1-chlorobutane was performed using AP-MgO as a catalyst; And 1-butene is the selective product formed even after several cycles of 1-chlorobutane injections. AP-MgO was allowed to react with Cl2, which resulted in the formation of a highly reactive adduct which has a capability to selectively chlorinate propane.
Библиографическая ссылка:
Richards R.
, Mulukutla R.S.
, Mishakov I.
, Chesnokov V.
, Volodin A.
, Zaikovski V.
, Sun N.
, Klabunde K.J.
Nanocrystalline Ultra High Surface Area Magnesium Oxide as a Selective Base Catalyst
Scripta Materialia. 2001. V.44. N8-9. P.1663-1666. DOI: 10.1016/S1359-6462(01)00877-6 WOS Scopus РИНЦ
Nanocrystalline Ultra High Surface Area Magnesium Oxide as a Selective Base Catalyst
Scripta Materialia. 2001. V.44. N8-9. P.1663-1666. DOI: 10.1016/S1359-6462(01)00877-6 WOS Scopus РИНЦ
Даты:
Поступила в редакцию: | 21 авг. 2000 г. |
Принята к публикации: | 22 нояб. 2000 г. |
Опубликована в печати: | 18 мая 2001 г. |
Опубликована online: | 13 июн. 2001 г. |
Идентификаторы БД:
Web of science | WOS:000169389400099 |
Scopus | 2-s2.0-0035906768 |
РИНЦ | 13385558 |
Chemical Abstracts | 2001:440766 |
Chemical Abstracts (print) | 135:127683 |
OpenAlex | W1983987673 |